1) solidified velocity
凝固冷却速度
1.
At different solidified velocity, the change of microstructure and performance on magnesium alloy anode has been studied.
论文研究了不同凝固冷却速度下,镁合金阳极显微组织和性能的变化。
3) cooling velocity
冷却速度
1.
Influence of cooling velocity after coiling on the structure of high strength steel;
卷取后冷却速度对高强度热轧带钢组织的影响
2.
The results show that,when cooling velocity increases,the beginning temperature and the finishing temperature of phase transformation are both decrease,the grain is obviously refined.
结果表明:随着冷却速度的增大,相变开始温度和结束温度均降低,晶粒明显被细化。
3.
The effect of two cooling velocity on strain-aging sensibility of 16MnR hot rolled steel plate has been studied.
研究了2种冷却速度对16MnR热轧钢板应变时效敏感性的影响。
4) Cooling Rate
冷却速度
1.
Effect of Cooling Rate on Structure Evolution of Hot Deformed Ferrite-Bainite Micro Alloying Steel;
热变形后冷却速度对铁素体-贝氏体微合金钢组织演变的影响
2.
Eeffects of cooling rate on solidification structures of Al-Si-Cu sputtering targets;
冷却速度对Al-Si-Cu溅射靶材凝固组织的影响
3.
Effects of Cooling Rate on the Microstructure and Properties of Cu-Cr Alloy;
冷却速度对Cu-Cr合金组织和性能的影响
5) cooling speed
冷却速度
1.
In this paper,impact on phase transformation speed and formation produced by different cooling speed between 10k/min and 200k/min in the cooling process of steel T91 has been investigated.
本文研究了T91钢冷却过程中,不同冷却速度(10k/min(200k/min)对相变速度和产物的影响。
2.
The test shows that the cooling speed affects the first arm-spacing and the second arm-spacing, and concluded that they are decreased, the fracture fractographies are improved, and the mechanical properties, especially the toughness, is obviously increased while the cooling speed increases.
试验表明,冷却速度增大,使奥氏体的一次二次枝晶间距缩小,断口形貌改善;并且可使材质的综合力学性能,特别是韧性明显提高。
3.
To research the effect of different cooling speed on the microstructure and property of 9 mm high carbon steel wire rod by means of cooling control process and the experiments of microstructure and property and the simulated analysis.
通过控冷工艺、组织性能实验和模拟分析 ,研究了不同冷却速度对 9mm高碳钢线材组织性能的影响。
6) cooling rates
冷却速度
1.
Influence of cooling rates on the morphology of pearlite in Fe-0.12%C alloy under high magnetic field
强磁场下冷却速度对Fe-0.12%C合金显微组织的影响
2.
The influence of casting temperature,cooling rates,reheating temperature and time on liquidus casting microstructure was investigated.
采用液相线铸造法即在液相线温度铸造变形铝合金２６１８获得了金属半固态加工要求的细小、等轴的“非枝晶”组织，同时考察了铸造温度、冷却速度及再加热温度和时间对该组织的影响·结果表明，在一定冷却速度条件下在液相线温度铸造能获得适合于半固态加工的细小球形晶粒，并且该组织在再加热回半固态仍能保持稳定
3.
In the paper, the research of pouring temperatures and cooling rates on the alloy s solidifying microstructures has been studied with AlSi7Mg alloy.
以AlSi7Mg合金为例,研究熔体的浇注温度和冷却速度对其凝固组织的影响。
补充资料：迟延凝固剂
分子式：
CAS号：
性质：又称胶凝剂。加入胶乳中，能使胶乳从液态转变为均匀的半刚性固体凝胶，而且保持原有形状及大小的物质。迟延凝固剂常用的有硅氟化钠，碱性的钛、锆与硼的氟化物等。多用于胶乳泡沫制品的加工，以氟硅酸盐(如氟硅酸钠、氟硅酸钾)的应用最为普遍。
CAS号：
性质：又称胶凝剂。加入胶乳中，能使胶乳从液态转变为均匀的半刚性固体凝胶，而且保持原有形状及大小的物质。迟延凝固剂常用的有硅氟化钠，碱性的钛、锆与硼的氟化物等。多用于胶乳泡沫制品的加工，以氟硅酸盐(如氟硅酸钠、氟硅酸钾)的应用最为普遍。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条