1) deep-drawing sheet
深冲压板
2) deep drawing
深冲
1.
Research on annealing process of 2B06-O aluminium alloy sheets for deep drawing;
深冲用2B06-O铝合金板材的工艺研究
2.
In this article we describe the development and characteristics of deep drawing quality hot dip galvanizing strip and analyze the influence of processing values on product properties, give the main points on controlling the quality of products.
阐述了深冲热镀锌板的发展趋势和生产工艺特点。
3.
The effects of different anisotropic yield criteria(Hill1948,Barlat YLD91 and CMTP) on the deep drawing simulation of a circular blank sheet based on FEM were studied,and the numerical solution of different yield functions was compared with each other.
基于板料成形深冲过程的数值模拟,研究了不同的各向异性屈服准则(Hill1948,Barlat YLD91和CMTP)对铝合金板深冲成形过程起皱预测的影响,并对模拟结果进行了比较,结果表明:采用不同屈服准则模拟的应力和应变分布有所不同,采用CMTP和Balart YLD91屈服准则比Hill1948屈服准则预测的要高。
3) deep-drawing
深冲
1.
The effect of rolling process on the microstructure and mechanical properties of deep-drawing molybdenum strip was investigated in this paper through changing rolling temperature and rolling process.
通过轧制温度、轧制方式实验,以及织构和力学性能分析,研究了轧制工艺对液晶显示背光源用的深冲钼带的组织和性能的影响。
4) deep drawability
深冲性能
1.
The effects of processing parameters of ferritic rolling on microstructures and mechanical properties especially on deep drawability of ultra-low carbon and Ti-stabilized interstitial-free steels were investigated,and the precipitates in Ti-IF steel were also analyzed.
本文研究了铁素体区轧制工艺条件对超低碳(ULC)钢和钛处理的无间隙原子(Ti-IF)钢组织和性能,特别是对深冲性能的影响,并分析了Ti-IF钢中的析出物。
2.
The cross-section metallurgic structure at various annealing temperature is analyzed and compared with import material based on the statistical study of the influence of annealing temperature on the deep drawability of cold rolled IF steel.
在统计分析退火温度对冷轧 IF 钢深冲性能的影响的基础上,对不同退火温度下的断面金相组织亦进行了分析,并与进口料进行了对比。
5) drawability
深冲性能
1.
The effect of the reduction in cold rolling IF steel sheet for drawability;
冷轧压下率分配对IF钢深冲性能的影响
2.
The results showed that the IF steel has better deep drawability,higher mechanical and texture strength and elongation if the hot rolling temperature was low with big reduction in ferrite region.
结果表明,较低的铁素体轧制温度和较高的铁素体区压下量时,IF钢具有更高的深冲性能、相对较高的强度、延伸率以及织构强度。
3.
How the processing conditions affect the properties especially the drawability of a ferritic hot-rolled and annealed Ti-IF sheet steel was investigated.
研究了铁素体轧制工艺条件对一种Ti-IF钢的性能,特别是深冲性能的影响。
6) deep-drawing property
深冲性能
1.
Effect of cold rolling-process on microstructure and deep-drawing property of 1050H19 aluminum foils used in air-conditioner;
冷轧工艺对1050H19空调箔微观结构及深冲性能的影响
2.
The relationship of deep-drawing property and rolling parameters of IF steel was researched by the testing of ferritic rolling and annealing.
通过对IF钢铁素体区轧制、退火工艺的研究及对塑性应变比r值的检测,并结合对取向分布函数图的定量分析,研究了深冲性能与轧制工艺参数的关系。
参考词条
补充资料：板料多步冲压回弹的数值模拟研究
摘 要：回弹是板料冲压成形过程中一种常见但很难解决的现象。首先研究了板料弯曲变形中卸载回弹的原理，然后以依维柯侧壁上内板为例，采用动态和静态算法相结合的方法，在考虑每道工序板料回弹的基础上，对其进行多步冲压回弹的数值模拟，最后对模拟结果和实验结果进行比较，验证该模拟方法提高回弹计算精度的有效性，为板料冲压成形工艺的制定提供科学依据。 关键词：回弹；多步冲压；数值模拟
1 前 言
通常，一个完整的冲压过程要经过拉延、整形、修边、冲孔、翻边等多步工序才能完成。在这一过程中，回弹是板料成形工艺制定中要考虑的关键因素，零件的最终形状取决于成形后的回弹量，当回弹量超过允许容差后，就成为成形缺陷，影响零件的几何精度。特别是近几年来由于高强度薄钢板和铝合金板材的大量使用，回弹问题更为突出。
目前，板料回弹的精确预测以及如何减小回弹量、降低残余应力成为板料成形模拟中的热点问题。从NUMISHEET’93（第二届板料成形三维数值模拟国际会议）开始，每届会议都有关于回弹预测的标准考题（BENCHMARK），在NUMISHEET’99上，专门有一个关于回弹预测和回弹误差控制的会议专题，其中文章达到10篇，约占全部会议文章的11﹪；而在NUMISHEET’2002上，关于回弹预测和控制的会议专题论文达20篇之多，占到全部会议论文的21﹪以上。
在实际生产中要控制和补偿回弹，提高回弹预测的精度是至关重要的。通常我们在进行板料多步冲压的回弹预测时，都忽略了板料每道工序后的卸载回弹，未将其回弹考虑到下一道工序的计算之中，然而板料的最终形状是其整个变形历史的累积效应，其变形历史等对残余应力和回弹计算都有一定影响，那么因忽略了每道工序后的回弹而产生的累积误差势必影响最终的回弹预测精度。
本文在进行板料多步冲压数值模拟时以依维柯侧壁上内板为例，采用动态和静态算法相结合的方法来模拟其多步冲压过程，将前一道工序的回弹计算结果作为下一道工序的输入，并通过模拟结果和实验结果的对比来验证该数值模拟过程的正确性及有效性。
2 板料多步冲压回弹的数值模拟研究
2.1板料卸载回弹的原理研究
板料在外载荷作用下发生任何一种塑性变形时，其变形都是由塑性变形和弹性变形两部分组成。当作用板料上的外载荷卸掉之后，塑性变形区的材料保存残余变形而使零件变形。但是，由于弹性变形区材料的弹性恢复以及塑性变形区材料弹性变形部分的弹性恢复，使其形状、尺寸都发生与加载时变形方向相反的变化，这种现象称之为回弹。这就是生产中回弹现象的内因。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。