1) solidification rate
凝固速率
1.
The empirical results indicate that the increase of solidification rate can achieve intermetallic particles reinforced phase with ideal morphological features in Al-Ni alloy.
实验结果表明,提高凝固速率可以使Al-Ni合金获得理想形貌的金属间化合物强化相。
2.
Exporimental results show that the stress- rupture life of DZ22 at 980℃ and 220 MPa was increased from 71 hours and 50 nunutes to 168 hours and 5 minutes at relatively high solidification rate.
本文采用ＺＭＬＭＣ超高梯度定向凝固法（ＺＭＬＭＣ法），研究了两种凝固速率下ＤＺ２２合金的高温力学性能和组织。
3.
The dendritic arm spacings and microsegregations of directionally solidified superalloy DZ22 at various solidification rates have been studied with the help of a ZMLMC directional solidification equipment.
采用新研制的超高梯度定向凝固装置，研究了不同凝固速率下定向凝固高温合金ＤＺ２２的枝晶臂间距和枝晶偏析。
2) rate/quick quenching
速率/快速凝固
3) rapid solidification
快速凝固
1.
Rapid Solidification of Cu-10Ag Alloy Droplets by Ultrasonic Arc Spray Atomization;
超音速电弧喷射雾化Cu-10Ag合金熔滴的快速凝固
2.
Carbide and its stability in FGH95 superalloy powders during rapid solidification;
快速凝固FGH95合金粉末中的碳化物及其稳定性
3.
Microstructure evolution of hypereutectic Al-Si alloy during rapid solidification;
过共晶Al-Si合金快速凝固组织演变
4) solidification rate
凝固速度
1.
Influence of solidification rate on solid-liquid interface in unidirectional solidification microstructure of austenitic stainless steel
凝固速度对奥氏体不锈钢定向凝固组织及其固液界面稳定性的影响
2.
The percentage of RE in the matrix increases with the increase of solidification rate; the carbides in directional solidification microstructure are refined by RE added in high chromium cast iro.
研究表明,稀土主要位于高铬铸铁的基体组织中,随凝固速度的增加,稀土在基体中的含量增加;稀土对高铬铸铁定向凝固组织中的碳化物具有细化作用,并随凝固速度的增加,定向凝固高铬铸铁组织细化程度提高,同时稀土的加入使高铬铸铁的抗拉强度明显提高。
3.
The microstructure and its evolution of directionally solidified Cu-Cr alloy were investigated under the condition of different solidification rates,by use of optical microscope and SEM.
在高梯度定向凝固装置上制备Cu-1·0%Cr(质量分数)合金,用金相显微镜、扫描电镜进行微观组织的观察,研究定向凝固速度对Cu-Cr合金微观组织形貌的影响。
5) rapidly solidification
快速凝固
1.
Microstructure and property of Mg_(80)Cu_(15)Y_5 alloy by rapidly solidification and hot extrusion
热挤压快速凝固Mg_(80)Cu_(15)Y_5合金棒材的组织与性能
2.
The effects of rapidly solidification on the microstructure and the corrosion behavior of Mg-5Zn-1Y-0.
研究了快速凝固Mg-5Zn-1Y-0。
6) melt spinning
快速凝固
1.
3～1) are prepared by means of vacuum arc melting followed by high temperature annealing and quenching or melt spinning method.
0)在常规熔铸、高温退火+淬火及快速凝固不同制备条件下的组织结构和电化学性能。
2.
4 were prepared using conventional cast, rapid solidification (melt spinning) and annealing processes.
4 在常规熔铸、快速凝固、退火处理不同制备条件下的组织结构和电化学性能。
补充资料：自然凝固
分子式：
CAS号：
性质：指胶乳从胶树流出后、在不经任何处理的自然条件下，由于微生物和酶的作用而产生的凝固现象。通常胶乳从胶树流出后4h就会发生自然凝固。
CAS号：
性质：指胶乳从胶树流出后、在不经任何处理的自然条件下，由于微生物和酶的作用而产生的凝固现象。通常胶乳从胶树流出后4h就会发生自然凝固。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条