1) dewfall rate
凝露速率
2) solidification rate
凝固速率
1.
The empirical results indicate that the increase of solidification rate can achieve intermetallic particles reinforced phase with ideal morphological features in Al-Ni alloy.
实验结果表明,提高凝固速率可以使Al-Ni合金获得理想形貌的金属间化合物强化相。
2.
Exporimental results show that the stress- rupture life of DZ22 at 980℃ and 220 MPa was increased from 71 hours and 50 nunutes to 168 hours and 5 minutes at relatively high solidification rate.
本文采用ＺＭＬＭＣ超高梯度定向凝固法（ＺＭＬＭＣ法），研究了两种凝固速率下ＤＺ２２合金的高温力学性能和组织。
3.
The dendritic arm spacings and microsegregations of directionally solidified superalloy DZ22 at various solidification rates have been studied with the help of a ZMLMC directional solidification equipment.
采用新研制的超高梯度定向凝固装置，研究了不同凝固速率下定向凝固高温合金ＤＺ２２的枝晶臂间距和枝晶偏析。
3) agglomerating velocity
凝集速率
4) aggregate rate
凝聚速率
1.
An aggregate rate possibility model is established and the conclusions drawn from the study of the possibility model concerning various deposition rates are in full agreement with the experimental data.
从沉积在液体基底上银原子的凝聚实验规律出发，对凝聚机理进行研究，提出了凝聚速率的几率模型，给出了由该几率模型所得到的结论，并对不同沉积速率下所得到的结论与实验数据进行比较，得到与实验数据相一致的结果。
5) gelation rate
胶凝速率
1.
The gelation rate of the beads were measured in terms of weight changes.
以胶凝过程中凝胶微丸重量变化 (失水量 )研究了胶凝速率及不同浓度海藻酸钠溶液 ( 1 %～ 4 % )与氯化钙溶液 ( 0 0 5～0 2 0mol/L)对胶凝速率的影响 ,结果是 6h前胶凝速率快 ,随后减慢 ,约 70h胶凝完全 ,氯化钙溶液的浓度≥ 0 1mol/L对胶凝速率无明显影响。
6) flocculation in pipes
絮凝速率