1) TiO2 film
TiO2薄膜
1.
Nanometer scale TiO2 film was prepared on glass substrate with film thickness less than 100 nm,crystal size in the range of 10~30 nm by sol-gel process combining with spin-coating technology.
以玻璃为基底,采用溶胶-凝胶法,利用旋涂技术在玻璃表面制备了膜厚小于100 nm,粒径在10~30 nm之间的纳米TiO2薄膜;利用XRD,AFM系统研究了煅烧温度及膜厚对薄膜亲水性的影响。
2.
TiO2 film is prepared by the method of cathodic electrodeposition in peroxotitanium solution of pure TiCl4,and the mechanism and process condition of electrochemical deposition are studied.
使用TiCl4的前驱体溶液,采用阴极电沉积法在301不锈钢表面制备TiO2薄膜,并研究了电化学沉积过程的机理和工艺条件。
3.
TiO2 films were coated on the surface of carbon fibers by Sol-gel.
采用溶胶-凝胶法在炭纤维表面涂覆TiO2薄膜,通过球磨混合均匀、热压烧结制备炭纤维增强羟基磷灰石复合材料,用三点弯曲法测试复合材料的弯曲强度。
2) TiO2 thin film
TiO2薄膜
1.
TiO2 thin films were prepared by DC reactive magnetron sputtering with different oxygen partial pressures.
采用直流磁控溅射法在不同氧分压下制备TiO2薄膜;研究氧分压对TiO2薄膜的表面形貌、晶体结构、化学组分及光吸收性能的影响。
2.
Microporous TiO2 thin films were fabricated by the sol-gel method.
借调节sol-gel法中溶胶的pH值,薄膜的热处理温度,研究了它们对TiO2薄膜的晶相组成、晶粒大小、表面结构和紫外及可见光吸收性能的影响。
3.
The best photocatalytic ability was investigated in terms of the degradation of methyl orange on TiO2 thin film.
采用溶胶-凝胶法制备TiO2溶胶,将其涂覆在普通钠钙玻璃上,以TiO2对甲基橙的光分解率探讨TiO2薄膜最佳光催化性能。
3) TiO_2 thin film
TiO2薄膜
1.
The environmental material of TiO_2 thin film is prepared using ZDL-2051 automotive lighting vacuum metallising system with the method of vacuum evaporation deposition technique.
采用ZDL-2051型真空镀膜机,用真空蒸发沉积方法制备环保材料TiO2薄膜,并用扫描电子显微镜(SEM)和X射线能量色散谱仪对其表面形貌及成分分别进行了观察、分析和表征。
2.
The porous Mn~(2+)-doping TiO_2 thin films are prepared by a sol-gel technique on glass sheet.
采用溶胶-凝胶法制备Mn2+掺杂的TiO2薄膜光催化剂,进行甲醛的光催化实验,考察Mn2+掺杂量、薄膜焙烧温度、溶胶体系pH值及薄膜厚度对光催化性能的影响。
3.
TiO_2 thin films were deposited on different substrates in vacuum by way of cathode arc discharge.
在真空条件下利用真空电弧源在不同基底材料上镀制了TiO2薄膜。
4) TiO_2 film
TiO2薄膜
1.
Electrochromic TiO_2 films were prepared on the PET/ITO and Glass/ITO substrates by the sol-gel method.
4mol/L的溶胶可以通过多次提拉制得表面光洁的较厚透明TiO2薄膜;随热处理温度的升高,薄膜的电色可逆性变好,循环寿命变大,但离子储存能力下降;塑料基TiO2薄膜与相同条件下制备的玻璃基薄膜具有相似的性能,呈现出较弱的阴极电致变色效应和较强的Li+储存能力,有望用作柔性电致变色器件的对电极。
2.
It was introduced that fabrication process of the porous TiO_2 thin film by screen-printing technique and described the effects of PEG、H30、PS as materials for making pore in the pastes on TiO_2 films for dye-sensitized solar cell.
介绍了染料敏化太阳能电池中丝网印刷制备TiO2多孔薄膜的过程,论述胶体组成中具有造孔作用的PEG,H30,PS等化学物质对纳晶染料敏化太阳能电池中TiO2薄膜性能的影响,并详细阐述了三者造成影响的原因。
3.
Photocatalytic TiO_2 films were successfully prepared by DC reactive magnetron sputtering.
采用直流反应溅射技术可以制备出具有光催化作用的TiO2薄膜。
5) TiO_2 thin films
TiO2薄膜
1.
The developing methods of preparing TiO_2 thin films were reviewed.
论述了纳米TiO2薄膜制备技术的最新研究进展。
2.
Transparent TiO_2 thin films were obtained on glass by a liquid phase deposition method(LPD).
采用液相沉积法(LPD)在玻璃的表面制得透明的TiO2薄膜,以XRD和SEM等方法对薄膜的物相、结构、形貌和光催化性能进行表征。
3.
TiO_2 thin films were prepared on glass substrates by RF magnetron sputtering.
利用射频磁控溅射设备在玻璃基片上制备TiO2薄膜,采用AFM、UV-Vis分光光度、接触角测定仪等测试手段,研究基片温度对薄膜表面形貌、粗糙度和表面性能的影响。
6) TiO2/Al2O3 films
TiO2/Al2O3薄膜
1.
Anatase TiO2 and TiO2/Al2O3 films were successfully prepared on foam nickel substrates by sol-gel technique.
研究表明:泡沫镍负载的TiO2和TiO2／Al2O3薄膜具有良好的光催化活性,特别是TiO2／Al2O3薄膜具有更高的催化活性。
补充资料：CaO-TiO2-SiO2 ceramics
分子式：
CAS号：
性质：在CaO-TiO2-SiO2三元系统中以CaSiO3与TiO2或以CaTiSiO5与CaTiO3为基料的陶瓷材料。其结构特点是两种晶相共存，性能受晶相比例影响。配比可在一定范围内调节。主要原料为碳酸钙、二氧化钛、二氧化硅，加入少量改性添加剂，经配料、磨细、混合、成型、烧成等工序获得制品，也可先用碳酸钙和二氧化硅高温下合成硅酸钙，用碳酸钙、二氧化硅、二氧化钛高温下合成钛硅酸钙后再进行配料、烧成等，以确保两晶相共存。主要介电性能为：介电常数80～110，介质损耗角正切值(0.8～2.5)×10-4，介电常数温度系数(-450～+550)×10-6/℃。抗电温度(45～55)kV/mm，电阻率(1011～1012)Ω·cm。主要用作温度补偿型陶瓷电容器瓷料。
CAS号：
性质：在CaO-TiO2-SiO2三元系统中以CaSiO3与TiO2或以CaTiSiO5与CaTiO3为基料的陶瓷材料。其结构特点是两种晶相共存，性能受晶相比例影响。配比可在一定范围内调节。主要原料为碳酸钙、二氧化钛、二氧化硅，加入少量改性添加剂，经配料、磨细、混合、成型、烧成等工序获得制品，也可先用碳酸钙和二氧化硅高温下合成硅酸钙，用碳酸钙、二氧化硅、二氧化钛高温下合成钛硅酸钙后再进行配料、烧成等，以确保两晶相共存。主要介电性能为：介电常数80～110，介质损耗角正切值(0.8～2.5)×10-4，介电常数温度系数(-450～+550)×10-6/℃。抗电温度(45～55)kV/mm，电阻率(1011～1012)Ω·cm。主要用作温度补偿型陶瓷电容器瓷料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条