2) CTBN
液体端羧基丁腈橡胶
1.
CTBN MODIFIED BMI CONSTRUCTION ADHESIVE (Ⅱ)THE FORM AND PROPERTIES OF CTBN MODIFIED 1~#/DACPE;
液体端羧基丁腈橡胶改性双马来酰亚胺结构胶粘剂(Ⅱ)DACPE固化BMI体系胶粘剂的改性及形态结构
2.
Aminopolysiloxane and carboxy terminal butadiene-acrylonitrile (CTBN) were used to modify the epoxy resin system, and the heat-resistant epoxy adhesive cured at room temperature was prepared.
采用氨基硅油和液体端羧基丁腈橡胶(CTBN)对环氧树脂进行化学改性,制备出室温固化耐热环氧胶粘剂。
3) CTBN
端羧基液体丁腈橡胶
1.
Dicyclopentadiene bisphenol diyanate ester(DCPDCE) was modified by CTBN to improve its brittleness.
采用端羧基液体丁腈橡胶(CTBN)对双环戊二烯型氰酸酯树脂(DCPDCE)进行改性。
4) carboxyl liquid nitrile rubber
羧基液体丁腈橡胶
1.
Epoxy resin was modified with carboxyl liquid nitrile rubber and CTBN/EP prepolymer was synthesized.
用羧基液体丁腈橡胶(CTBN)对环氧树脂(EP)进行改性,合成CTBN/EP预聚物。
5) carboxyl nitrile rubber
羧基丁腈橡胶
1.
Preparation of powdered carboxyl nitrile rubber/polyvinyl chloride blend;
粉末羧基丁腈橡胶/聚氯乙烯共混胶的研制
2.
In this paper,we choose carboxyl nitrile rubber,polysulfide rubber and hydroxyl polysiloxane as toughners and evaluate the effect of toughened epoxy resin with impact strength,bend strength and tensile shear strength.
以羧基丁腈橡胶、聚硫橡胶和羟基聚硅氧烷为增韧剂,以冲击强度、弯曲强度和拉伸剪切强度来评价环氧树脂的增韧效果。
6) carboxylated nitrile rubber
羧基丁腈橡胶
1.
Vulcanization properties of carboxylated nitrile rubber;
羧基丁腈橡胶的硫化性能
2.
Microphase structure and dynamic mechanical properties of carboxylated nitrile rubber-based damping composites
羧基丁腈橡胶基阻尼复合材料的相态结构及动态力学性能
3.
The blends of chlorosulfonated polyethylene(CSM)and carboxylated nitrile rubber(XNBR) could be vulcanized during molding at 185 ℃× 60 min in the absence of any vulcanizing agent.
在没有任何硫化剂的条件下，氯磺化聚乙烯（ＣＳＭ）和羧基丁腈橡胶（ＸＮＢＲ）的共混物（质量比１∶１）能在１８５℃×６０ｍｉｎ下模压硫化。
补充资料：端羧基液体丁腈橡胶
分子式：
CAS号：
性质：丁二烯和丙烯腈采用过氧化戊二酸为引发剂、无水酒精或四氢呋喃为溶剂，通过自由基聚合制备的液体橡胶。聚合温度110～120℃，聚合时间4～6h，转化率70％。端羧基液体丁腈橡胶以甲苯二异氰酸酯+三(2-甲基氮丙啶)氧化膦(TDI=MAPO)为固化剂，制成的推进剂黏结剂在220℃下测得的力学性能良好。在胺的催化作用下液体环氧树脂交联固化端羧基液体丁腈橡胶，可制得具有最佳强度的硫化胶。端羧基液体丁腈橡胶还广泛作为粘接、密封、灌封、喷涂材料。
CAS号：
性质：丁二烯和丙烯腈采用过氧化戊二酸为引发剂、无水酒精或四氢呋喃为溶剂，通过自由基聚合制备的液体橡胶。聚合温度110～120℃，聚合时间4～6h，转化率70％。端羧基液体丁腈橡胶以甲苯二异氰酸酯+三(2-甲基氮丙啶)氧化膦(TDI=MAPO)为固化剂，制成的推进剂黏结剂在220℃下测得的力学性能良好。在胺的催化作用下液体环氧树脂交联固化端羧基液体丁腈橡胶，可制得具有最佳强度的硫化胶。端羧基液体丁腈橡胶还广泛作为粘接、密封、灌封、喷涂材料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。