1) hydroxyl-terminated polybutadiene/acrylonitrile rubber
![点击朗读](/dictall/images/read.gif)
端羟基液体丁腈橡胶
2) Liquid Hydroxy-Terminated Butadiene-Acrylonitrile (HTBN)
![点击朗读](/dictall/images/read.gif)
端羟基液态丁腈橡胶(HTBN)
3) hydroxyl-terminated nitrile rubber
![点击朗读](/dictall/images/read.gif)
端羟基丁腈橡胶
1.
The solution copolymerization of butadiene and acrylonitrile for the synthesis of hydroxyl-terminated nitrile rubber was studied with H2O2 as initiator and ethanol as solvent in a l0 L and a 50 L polymerization reactors.
在10L和50L不锈钢聚合釜中,以合成端羟基丁腈橡胶(HTBN)为目的,用H_2O_2作引发剂,乙醇作溶剂,研究了丁二烯(Bd)和丙烯腈(AN)的溶液共聚合。
2.
The hydroxyl-terminated poly(L-lactic acid) prepolymer is prepared by the melt direct polycondensation process with polyethylene glycol and L-lactic acid,and isocyanate-terminated nitrile rubber(ITBN) is synthesized with toluene-2,4-di-iso-cyanate(TDI),hydroxyl-terminated nitrile rubber(HTBN).
以聚乙二醇和L-乳酸直接熔融缩聚法制备端羟基聚L-乳酸预聚物(HO-PLLA-OH),以甲苯-2,4-二异氰酸酯(TDI)与端羟基丁腈橡胶(HTBN)进行反应,合成了端异氰酸酯基丁腈橡胶(ITBN),然后再将端羟基聚L-乳酸与端异氰酸酯基丁腈橡胶发生偶联反应,合成了乳酸-丁腈橡胶嵌段共聚物,其分子质量高于原料端羟基聚L-乳酸,分子质量分布也比端羟基聚L-乳酸宽。
4) CTBN
![点击朗读](/dictall/images/read.gif)
液体端羧基丁腈橡胶
1.
CTBN MODIFIED BMI CONSTRUCTION ADHESIVE (Ⅱ)THE FORM AND PROPERTIES OF CTBN MODIFIED 1~#/DACPE;
液体端羧基丁腈橡胶改性双马来酰亚胺结构胶粘剂(Ⅱ)DACPE固化BMI体系胶粘剂的改性及形态结构
2.
Aminopolysiloxane and carboxy terminal butadiene-acrylonitrile (CTBN) were used to modify the epoxy resin system, and the heat-resistant epoxy adhesive cured at room temperature was prepared.
采用氨基硅油和液体端羧基丁腈橡胶(CTBN)对环氧树脂进行化学改性,制备出室温固化耐热环氧胶粘剂。
5) CTBN
![点击朗读](/dictall/images/read.gif)
端羧基液体丁腈橡胶
1.
Dicyclopentadiene bisphenol diyanate ester(DCPDCE) was modified by CTBN to improve its brittleness.
采用端羧基液体丁腈橡胶(CTBN)对双环戊二烯型氰酸酯树脂(DCPDCE)进行改性。
6) amine terminated liquid nitrile rubber
![点击朗读](/dictall/images/read.gif)
端氨基液体丁腈橡胶
补充资料:液体丁腈橡胶
分子式:
CAS号:
性质:平均分子量小于1万的丁腈橡胶,呈液态。以过氧化氢异丙苯-乙二胺四乙酸钠-硫酸亚铁-雕白粉为引发剂,进行乳液聚合,聚合温度200℃,聚合时间4h,过氧化氢异丙苯分两次加入,胶液经真空脱气、凝聚、洗涤、干燥得到液体丁腈橡胶。其分子链中的丁二烯以反式1,4为主,两种链节呈无规分布。液体丁腈橡胶有良好的耐油性和黏着性,可与酚醛树脂、环氧树脂制成粘接力强、回弹性和耐油性好的胶黏剂。也可用作不抽出性专用增塑剂。
CAS号:
性质:平均分子量小于1万的丁腈橡胶,呈液态。以过氧化氢异丙苯-乙二胺四乙酸钠-硫酸亚铁-雕白粉为引发剂,进行乳液聚合,聚合温度200℃,聚合时间4h,过氧化氢异丙苯分两次加入,胶液经真空脱气、凝聚、洗涤、干燥得到液体丁腈橡胶。其分子链中的丁二烯以反式1,4为主,两种链节呈无规分布。液体丁腈橡胶有良好的耐油性和黏着性,可与酚醛树脂、环氧树脂制成粘接力强、回弹性和耐油性好的胶黏剂。也可用作不抽出性专用增塑剂。