1) CTBN
端羧基丁腈橡胶
1.
Curing Process and Properties of BCE/CTBN Blends;
双酚A型氰酸酯/端羧基丁腈橡胶共混物的制备工艺和性能
2.
Pre-reaction mechanism of epoxy resin(EP) and CTBN was verified by FT-IR,it was reason that the hydroxyl was formed by esterification reactions between carboxyl and epoxy group.
利用红外光谱确认了环氧树脂(EP)与端羧基丁腈橡胶(CTBN)的预聚反应机理是-COOH与环氧基进行酯化反应生成-OH基团,其最佳反应条件是70℃、3 h。
3.
In the room temperature,a modified epoxy resin(I) prepared from CTBN and epoxy resin AG-80 was mixed proportionately as component A,with the modified epoxy resin(II) from the reaction between silicon-boron resin and bisphenol-A epoxy resin.
用端羧基丁腈橡胶(CTBN)与环氧树脂AG-80反应制得改性环氧树脂(I);以硅硼树脂与双酚A型环氧树脂反应得到改性环氧树脂(Ⅱ);将改性环氧树脂(I)和(II)按比例在室温下充分混匀为A组分,把固化剂、阻燃剂等混配成B组分,将A和B组分按不同配比均匀混合配成灌封材料,并以IR、拉力机等仪器分别对改性树脂、灌封材料进行结构及力学性能的测试表征。
2) CTBN
液体端羧基丁腈橡胶
1.
CTBN MODIFIED BMI CONSTRUCTION ADHESIVE (Ⅱ)THE FORM AND PROPERTIES OF CTBN MODIFIED 1~#/DACPE;
液体端羧基丁腈橡胶改性双马来酰亚胺结构胶粘剂(Ⅱ)DACPE固化BMI体系胶粘剂的改性及形态结构
2.
Aminopolysiloxane and carboxy terminal butadiene-acrylonitrile (CTBN) were used to modify the epoxy resin system, and the heat-resistant epoxy adhesive cured at room temperature was prepared.
采用氨基硅油和液体端羧基丁腈橡胶(CTBN)对环氧树脂进行化学改性,制备出室温固化耐热环氧胶粘剂。
3) CTBN
端羧基液体丁腈橡胶
1.
Dicyclopentadiene bisphenol diyanate ester(DCPDCE) was modified by CTBN to improve its brittleness.
采用端羧基液体丁腈橡胶(CTBN)对双环戊二烯型氰酸酯树脂(DCPDCE)进行改性。
4) the liquid carboxyl-terminated butadiene-acrylonitrile (CTBN)
端羧基丁腈橡胶(CTBN)
5) carboxyl nitrile rubber
羧基丁腈橡胶
1.
Preparation of powdered carboxyl nitrile rubber/polyvinyl chloride blend;
粉末羧基丁腈橡胶/聚氯乙烯共混胶的研制
2.
In this paper,we choose carboxyl nitrile rubber,polysulfide rubber and hydroxyl polysiloxane as toughners and evaluate the effect of toughened epoxy resin with impact strength,bend strength and tensile shear strength.
以羧基丁腈橡胶、聚硫橡胶和羟基聚硅氧烷为增韧剂,以冲击强度、弯曲强度和拉伸剪切强度来评价环氧树脂的增韧效果。
6) carboxylated nitrile rubber
羧基丁腈橡胶
1.
Vulcanization properties of carboxylated nitrile rubber;
羧基丁腈橡胶的硫化性能
2.
Microphase structure and dynamic mechanical properties of carboxylated nitrile rubber-based damping composites
羧基丁腈橡胶基阻尼复合材料的相态结构及动态力学性能
3.
The blends of chlorosulfonated polyethylene(CSM)and carboxylated nitrile rubber(XNBR) could be vulcanized during molding at 185 ℃× 60 min in the absence of any vulcanizing agent.
在没有任何硫化剂的条件下，氯磺化聚乙烯（ＣＳＭ）和羧基丁腈橡胶（ＸＮＢＲ）的共混物（质量比１∶１）能在１８５℃×６０ｍｉｎ下模压硫化。
补充资料：羧基丁腈橡胶
分子式：
CAS号：
性质：又称高强度型橡胶。指由丁二烯、丙烯腈和不饱和酸(如丙烯酸、甲基丙烯酸)三元共聚制得的系列橡胶的总称。共聚物主链中约100～200个碳原子含一个羧基，在丁腈橡胶中引入羧基可提高其拉伸强度、抗撕裂强度、硬度、耐磨性、黏着性和抗臭氧老化性。还可增加与聚氯乙烯、酚醛树脂等的相容性。羧基丁腈橡胶主要用于制造胶管、胶带、密封件，O形圈、胶辊、胶鞋、各种模制品、油井专用品。还用于配制耐油胶黏剂。
CAS号：
性质：又称高强度型橡胶。指由丁二烯、丙烯腈和不饱和酸(如丙烯酸、甲基丙烯酸)三元共聚制得的系列橡胶的总称。共聚物主链中约100～200个碳原子含一个羧基，在丁腈橡胶中引入羧基可提高其拉伸强度、抗撕裂强度、硬度、耐磨性、黏着性和抗臭氧老化性。还可增加与聚氯乙烯、酚醛树脂等的相容性。羧基丁腈橡胶主要用于制造胶管、胶带、密封件，O形圈、胶辊、胶鞋、各种模制品、油井专用品。还用于配制耐油胶黏剂。