1) Fe-Al/WC composite coating
Fe-Al/WC复合涂层
1.
The Fe-Al/WC intermetallic composite coatings have been prepared by high velocity arc spraying (HVAS)technology on 20G steel and the anti-hot corrosion performance of Fe-Al/WC composite coatings at 450℃ has been studied by hot corrosion test.
结果表明,Fe-Al/WC复合涂层的热腐蚀动力学曲线近似呈现出抛物线规律;涂层表面的腐蚀产物主要为疏松的Fe2O3,此外,还有少量的Al2O3和FeS,且其分布不均匀;涂层表面优先形成具有保护性的Al2O3膜,保证了涂层具有一定的抗热腐蚀性能;Fe元素的扩散、化学反应及电化学反应综合作用是涂层加速腐蚀的主要原因。
2) Fe-Al/SiC composite coating
Fe-Al/SiC复合涂层
1.
Fe-Al/SiC composite coating was made by HVFS.
利用高速火焰喷涂技术制备出Fe-Al/SiC复合涂层,在MM-A1立式磨损试验机上对涂层常温下的摩擦磨损特性进行研究。
2.
It indicated that the matrix of Fe-Al/SiC composite coating was Fe-Al phase (Fe3Al,FeAl) and SiC hard phase distributed all over the coating, and the coating displayed the typical layers structure characteristics.
采用高速火焰喷涂技术制备了Fe-Al/SiC复合涂层,对涂层在650℃下的热腐蚀动力学规律进行了研究,并利用扫描电镜(SEM)、能谱仪(EDS)和X射线衍射仪(XRD)对涂层及腐蚀产物的成分和形貌进行分析。
3.
In order to solve the hot corrosion problem on the water-wall tubes in thermal power plants, HVFS technology was used to prepare the Fe-Al/SiC composite coating, and the bonding strength, micro hardness, thermal shock and hot corrosive resistance performance of the coating were studied.
为解决火电厂锅炉水冷壁热腐蚀问题,采用高速火焰喷涂技术首次制备出Fe-Al/SiC复合涂层,并对涂层的结合强度、显微硬度、抗热震性能和耐热腐蚀性能进行了研究。
3) Fe-Al/Cr_3C_2 composite coating
Fe-Al/Cr3C2复合涂层
4) iron-aluminide and alumina composite coating
Fe-Al/Al2O3复合涂层
补充资料：[3-(aminosulfonyl)-4-chloro-N-(2.3-dihydro-2-methyl-1H-indol-1-yl)benzamide]
分子式：C16H16ClN3O3S
分子量：365.5
CAS号：26807-65-8
性质：暂无
制备方法：暂无
用途：用于轻、中度原发性高血压。
分子量：365.5
CAS号：26807-65-8
性质：暂无
制备方法：暂无
用途：用于轻、中度原发性高血压。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条