1) Al-Si eutectic alloy
铝硅共晶合金
1.
The size distribution of the powder solder for Al-Si eutectic alloy using gas atomization;
空气流雾化铝硅共晶合金粉末钎料的粒度分布
2.
This paper reports effects of Lanthanide Fluoride as additions on the mechanical property and microstructure of Al-Si eutectic alloy.
研究了氟化镧对ZAlSi12合金的变质作用,发现氟化镧可使铝硅共晶合金达到完全变质并且具有良好的长效性和抗衰退性,同时大大提高合金的抗拉强度和延伸率。
2) Hypoeutectic Al-Si Alloy
亚共晶铝硅合金
1.
Semi-solid slurry of hypoeutectic Al-Si alloy was prepared by the means of low temperature pouring,and the morphology of semi-solid primary phase and its fractal dimension as well as the corresponding computation were researched.
利用低过热度浇注技术制备了亚共晶铝硅合金半固态浆料,研究了半固态初生相的形貌及其分形维数和计算方法。
3) hypereutectic Al Si alloy
过共晶铝硅合金
1.
The results of experiment show the average grain size of primary Si phase in hypereutectic Al Si alloy is changed to 35?μm from 250?μm, σ b is changed to 236?MPa from 178?MPa.
研究了复合变质对过共晶铝硅合金组织和性能的影响 ,实验结果表明 :经采用ZXH复合变质剂变质处理后 ,过共晶铝硅合金中的初晶硅晶粒平均尺寸由变质前的 2 5 0 μm变为 35 μm ,抗拉强度由变质前的 178MPa提高到2 36MPa ,冲击韧度由变质前的 7J/cm2 提高到 15 。
5) hypereutectic Al-Si alloy
过共晶铝-硅合金
6) Al Si eutertic alloy
铝-硅共晶合金
补充资料：铝-硅系铸造铝合金
分子式：
CAS号：
性质：以硅为主要合金元素的铸造铝合金。硅的添加量范围为5％～25％，并添加镁、铜等元素，形成亚共晶型、共晶型或过共晶型合金。含硅量为5％～13％的亚共晶型或共晶型合金是工业生产中应用最广泛的铸造铝合金。良好的铸造工艺性能和气密性是它们的主要特点。含硅量在13％以上的过共晶型合金具有热膨胀系数小、耐磨性好等特点。
CAS号：
性质：以硅为主要合金元素的铸造铝合金。硅的添加量范围为5％～25％，并添加镁、铜等元素，形成亚共晶型、共晶型或过共晶型合金。含硅量为5％～13％的亚共晶型或共晶型合金是工业生产中应用最广泛的铸造铝合金。良好的铸造工艺性能和气密性是它们的主要特点。含硅量在13％以上的过共晶型合金具有热膨胀系数小、耐磨性好等特点。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。