1) hyper-eutectic Al-Si alloys
过共晶硅铝合金
1.
According to the research focus of spray-forming technology at present, the study of spray-forming Al alloys such as ultra-high strength and toughness Al alloys,heat-resistant Al alloys,hyper-eutectic Al-Si alloys and electronic-packaging Si-Al alloys was introduced.
根据目前喷射沉积技术的研究热点,主要介绍喷射沉积铝合金材料,如超高强/高韧铝合金、耐热铝合金、过共晶硅铝合金、电子封装Si-Al合金等新型高性能轻质材料的一些研究现状。
2) hypereutectic Al Si alloy
过共晶铝硅合金
1.
The results of experiment show the average grain size of primary Si phase in hypereutectic Al Si alloy is changed to 35?μm from 250?μm, σ b is changed to 236?MPa from 178?MPa.
研究了复合变质对过共晶铝硅合金组织和性能的影响 ,实验结果表明 :经采用ZXH复合变质剂变质处理后 ,过共晶铝硅合金中的初晶硅晶粒平均尺寸由变质前的 2 5 0 μm变为 35 μm ,抗拉强度由变质前的 178MPa提高到2 36MPa ,冲击韧度由变质前的 7J/cm2 提高到 15 。
4) hypereutectic Al-Si alloy
过共晶铝-硅合金
5) Hypereutectic Al-Si Alloy
过共晶铝硅合金
1.
Microstructure and Properties of Hypereutectic Al-Si Alloy by Laser Surface Remelting;
激光表面重熔过共晶铝硅合金的组织与性能
2.
Research on Compound Processing of Preparation of Hypereutectic Al-Si Alloy;
复合处理制备半固态过共晶铝硅合金的研究
3.
Influence of Solution Treatment on Microstructure and Properties of Rapidly Solidified Hypereutectic Al-Si Alloys
固溶处理对快速凝固过共晶铝硅合金组织性能的影响
6) A390 alloy
A390过共晶高硅铝合金
1.
Influence of Bi element on the frictional behavior of A390 alloy was investigated in this paper.
采用自行改制的MM-200型摩擦磨损试验机研究了Bi对A390过共晶高硅铝合金摩擦磨损性能的影响规律。
补充资料：铝-硅系铸造铝合金
分子式：
CAS号：
性质：以硅为主要合金元素的铸造铝合金。硅的添加量范围为5％～25％，并添加镁、铜等元素，形成亚共晶型、共晶型或过共晶型合金。含硅量为5％～13％的亚共晶型或共晶型合金是工业生产中应用最广泛的铸造铝合金。良好的铸造工艺性能和气密性是它们的主要特点。含硅量在13％以上的过共晶型合金具有热膨胀系数小、耐磨性好等特点。
CAS号：
性质：以硅为主要合金元素的铸造铝合金。硅的添加量范围为5％～25％，并添加镁、铜等元素，形成亚共晶型、共晶型或过共晶型合金。含硅量为5％～13％的亚共晶型或共晶型合金是工业生产中应用最广泛的铸造铝合金。良好的铸造工艺性能和气密性是它们的主要特点。含硅量在13％以上的过共晶型合金具有热膨胀系数小、耐磨性好等特点。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条