1) A390 alloy
A390过共晶高硅铝合金
1.
Influence of Bi element on the frictional behavior of A390 alloy was investigated in this paper.
采用自行改制的MM-200型摩擦磨损试验机研究了Bi对A390过共晶高硅铝合金摩擦磨损性能的影响规律。
2) hypereutectic Al Si alloy
过共晶铝硅合金
1.
The results of experiment show the average grain size of primary Si phase in hypereutectic Al Si alloy is changed to 35?μm from 250?μm, σ b is changed to 236?MPa from 178?MPa.
研究了复合变质对过共晶铝硅合金组织和性能的影响 ,实验结果表明 :经采用ZXH复合变质剂变质处理后 ,过共晶铝硅合金中的初晶硅晶粒平均尺寸由变质前的 2 5 0 μm变为 35 μm ,抗拉强度由变质前的 178MPa提高到2 36MPa ,冲击韧度由变质前的 7J/cm2 提高到 15 。
4) hypereutectic Al-Si alloy
过共晶铝-硅合金
5) Hypereutectic Al-Si Alloy
过共晶铝硅合金
1.
Microstructure and Properties of Hypereutectic Al-Si Alloy by Laser Surface Remelting;
激光表面重熔过共晶铝硅合金的组织与性能
2.
Research on Compound Processing of Preparation of Hypereutectic Al-Si Alloy;
复合处理制备半固态过共晶铝硅合金的研究
3.
Influence of Solution Treatment on Microstructure and Properties of Rapidly Solidified Hypereutectic Al-Si Alloys
固溶处理对快速凝固过共晶铝硅合金组织性能的影响
6) hyper-eutectic Al-Si alloys
过共晶硅铝合金
1.
According to the research focus of spray-forming technology at present, the study of spray-forming Al alloys such as ultra-high strength and toughness Al alloys,heat-resistant Al alloys,hyper-eutectic Al-Si alloys and electronic-packaging Si-Al alloys was introduced.
根据目前喷射沉积技术的研究热点,主要介绍喷射沉积铝合金材料,如超高强/高韧铝合金、耐热铝合金、过共晶硅铝合金、电子封装Si-Al合金等新型高性能轻质材料的一些研究现状。
补充资料：铝合金的羽毛状晶
铝合金的羽毛状晶
feathey crystal of aluminium alloy
IUheJ旧deyumooZhuangJ旧g铝合金的羽毛状晶(feathey Crystal of alu-minium anoy)铝合金铸锭中柱状晶的变种，形状类似羽毛的晶粒。是铸锭缺陷的一种。形状近似直线状花边的羽毛状晶亦称为“花边状组织”。羽毛状晶成群出现，每群中羽毛状晶之间近似平行。羽毛状晶是双晶，以(111)晶面为双晶面。铝一镁系合金中的羽毛状晶如图所示。’ 产生羽毛状晶的工艺因素主要是:(1)熔体处于高温平稳状态，有较好的定向结晶条件。(2)在铸造温度下熔体停留时间过长，熔体过热和高度净化，减少结晶前沿形成晶核的数量。(3)合金中加入某些容易产生羽毛状晶的微量元素，如硼和错。 超硬铝合金、工业纯铝和高镁铝合金形成羽毛状晶的几率较大，而高强锻造铝合金2A70(LD7)、防锈铝合金 3A21(LF21)和含镁低于5%的铝镁系合金，基本上不形成羽毛状晶。 铸锭中存在羽毛状晶对其性能影响较大。在塑性加工过程中易在羽毛状晶的双晶面处产生裂纹。制品中残留的未完全破碎的羽毛状晶区会扩大使用性能的各向异性。蘸: 铝一镁系合金铸锭中的羽毛状晶偏光只100 (格长清)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。