1) modification/hypereutectic aluminum silicon alloy
变质处理/过共晶铝硅合金
2) hypereutectic Al Si alloy
过共晶铝硅合金
1.
The results of experiment show the average grain size of primary Si phase in hypereutectic Al Si alloy is changed to 35?μm from 250?μm, σ b is changed to 236?MPa from 178?MPa.
研究了复合变质对过共晶铝硅合金组织和性能的影响 ,实验结果表明 :经采用ZXH复合变质剂变质处理后 ,过共晶铝硅合金中的初晶硅晶粒平均尺寸由变质前的 2 5 0 μm变为 35 μm ,抗拉强度由变质前的 178MPa提高到2 36MPa ,冲击韧度由变质前的 7J/cm2 提高到 15 。
4) hypereutectic Al-Si alloy
过共晶铝-硅合金
5) Hypereutectic Al-Si Alloy
过共晶铝硅合金
1.
Microstructure and Properties of Hypereutectic Al-Si Alloy by Laser Surface Remelting;
激光表面重熔过共晶铝硅合金的组织与性能
2.
Research on Compound Processing of Preparation of Hypereutectic Al-Si Alloy;
复合处理制备半固态过共晶铝硅合金的研究
3.
Influence of Solution Treatment on Microstructure and Properties of Rapidly Solidified Hypereutectic Al-Si Alloys
固溶处理对快速凝固过共晶铝硅合金组织性能的影响
6) hyper-eutectic Al-Si alloys
过共晶硅铝合金
1.
According to the research focus of spray-forming technology at present, the study of spray-forming Al alloys such as ultra-high strength and toughness Al alloys,heat-resistant Al alloys,hyper-eutectic Al-Si alloys and electronic-packaging Si-Al alloys was introduced.
根据目前喷射沉积技术的研究热点,主要介绍喷射沉积铝合金材料,如超高强/高韧铝合金、耐热铝合金、过共晶硅铝合金、电子封装Si-Al合金等新型高性能轻质材料的一些研究现状。
补充资料：变质硅铝明
分子式：
CAS号：
性质：在熔炼过程中进行了变质处理的硅铝明。在含有11%～13%硅的简单硅铝明中加入2%～3%钠盐变质剂，可使粗大的针状共晶硅细化成分枝较多的细条状或点状，防止初晶硅析出，并出现初晶及固溶体，从而改善了组织，提高了性能，加入少量锑、锶、铋等也可对硅铝明起到变质作用。
CAS号：
性质：在熔炼过程中进行了变质处理的硅铝明。在含有11%～13%硅的简单硅铝明中加入2%～3%钠盐变质剂，可使粗大的针状共晶硅细化成分枝较多的细条状或点状，防止初晶硅析出，并出现初晶及固溶体，从而改善了组织，提高了性能，加入少量锑、锶、铋等也可对硅铝明起到变质作用。