2) polyaniline membrane
聚苯胺膜层
3) Reducted) polyaniline-intercalated graphite oxide nanocomposite ((R-(PAI/GO)
还原聚苯胺插层氧化石墨纳米材料
5) Intercalative polymerization
插层聚合
1.
Polyaniline/monmorillonite(PAN/MMT) composite was prepared by intercalative polymerization,which is characterized by XRD and FT-IR spectra.
运用插层聚合的方法制备了蒙脱土/聚苯胺复合材料,并进行了表征。
2.
A kind of polyurethane/ montmorillonite (PU/MMT) nanocomposite based on poly (propylene glycol)(PPG) and toluene-diisocyanate(TDI)was synthesized by intercalative polymerization technology and the function of shear stress of cone grinder.
借助锥体磨的研磨剪切外力,将聚醚多元醇插层进入蒙脱土片层中,使其片层间距扩大并发生部分剥离,从而利用本体插层聚合法制备了综合性能优异的聚氨酯/蒙脱土纳米复合弹性体材料。
3.
PET/MMT nanocomposites were prepared by intercalative polymerization technology.
采用烷基季铵盐对蒙脱土(MMT)进行有机化处理,采用插层聚合法制备PET/MMT纳米复合材料。
6) intercalation polymerization
插层聚合
1.
The method of preparation by melt blend is compared with intercalation polymerization.
综述了尼龙6/蒙脱土纳米复合材料的制备、结构、性能及应用,比较了插层聚合法和熔融共混法2种制备工艺,介绍了蒙脱土来源、尼龙品种对复合材料结构及性能的影响。
2.
Single-component PU/OMMT waterproof nano-coating were prepared by intercalation polymerization and the influence of OMMT amount on structure and property of nano-coatings were studied.
采用插层聚合法制备单组分聚氨酯/蒙脱土(PU/OMMT)纳米复合防水涂料,并研究蒙脱土用量对涂料的结构与性能的影响。
补充资料：聚三聚氰酸三烯丙酯层合板
分子式：
CAS号：
性质： 以聚三聚氰酸三烯丙酯为基料，玻璃布为增强材料制得的层合塑料。热稳定性和机械强度好，260℃下仍很稳定，且拉伸强度下降不多，而拉伸模量不变。但聚合物与玻璃布黏结力较差，层合板易分层。平纹玻璃布层合板拉伸强度室温下约250MPa，260℃时约200MPa；单向玻璃布层合板分别约为300MPa和230MPa，而拉伸模量在室温和260℃下，均为3.0×104Mpa。将充分浸渍聚三聚氰酸三烯丙酯后的玻璃布叠层至一定厚度，并在加压、加热下层合即得。主要用作绝缘板和装饰板，用于电子工业和装饰业。