1) multiaxial proportional loading
![点击朗读](/dictall/images/read.gif)
多轴比例加载
1.
Fatigue tests of 6063 aluminium alloy were performed under multiaxial proportional loading,and the fatigue characterristics and microcosmic mechanism were analyzed.
对6063铝合金进行多轴比例加载疲劳试验及微观结构观察,分析材料的疲劳特性及其微观机理。
2) multi-axial non-proportional loading
![点击朗读](/dictall/images/read.gif)
多轴非比例加载
1.
The fatigue damage of guyed mast\'s ear-plate\'s multi-axial non-proportional loading based on critical plane method was evaluated.
结果表明,临界面法更符合纤绳节点板多轴非比例加载的实际情况,因而可以给出更加合理的结果。
3) triaxial proportional loading
![点击朗读](/dictall/images/read.gif)
三轴比例加载
1.
Based on the Simpson integral method,the damage curve of concrete in the main stress direction under triaxial proportional loading is calculated by the damage model.
利用由Simpson积分方法建立的损伤模型,计算得到了混凝土在三轴比例加载作用下,竖向主应力方向的损伤曲线。
4) Proportional loading
![点击朗读](/dictall/images/read.gif)
比例加载
1.
Multiaxial fatigue behavior of superalloy GH4169 was investigated by using the thin tubular multiaxial fatigue specimens under proportional and non-proportional loadings at high temperature.
高温多轴疲劳试验采用比例与非比例加载路径。
2.
Biaxial fatigue behaviors of the Zr-4 alloy under proportional and non-proportional loading with the phase angles of 30°, 60° and 90° were studied.
研究了冷变形Zr-4合金在双轴比例和非比例加载下的循环变形行为,结果表明:当循环应变幅较低时,Zr-4合金表现为循环初始硬化随后饱和的特征;随着应变幅提高,初期硬化后,表现为连续循环软化特征;高应变幅下,初期硬化消失,表现为急剧的循环软化。
3.
The deformation behavior of hydrided zircaloy-4 under tension-torsion proportional loading was investigated using the quantitative metallography and the finite element method(FEM).
采用有限元数值分析方法,模拟了含氢化物Zr-4合金拉-扭双轴比例加载下的变形行为。
5) Proportional and nonproportional loading
![点击朗读](/dictall/images/read.gif)
比例加载与非比例加载
6) non-proportional loading
![点击朗读](/dictall/images/read.gif)
非比例加载
1.
Fatigue fracture characteristics of GH4169 super-alloy under non-proportional loading at high temperature;
GH4169合金高温多轴非比例加载下疲劳断口特征
2.
Investigation of fatigue damage parameters under multi-axial non-proportional loading;
![点击朗读](/dictall/images/read.gif)
多轴非比例加载条件下疲劳损伤参量的研究
3.
Multiaxial fatigue behavior of superalloy GH4169 was investigated by using the thin tubular multiaxial fatigue specimens under proportional and non-proportional loadings at high temperature.
高温多轴疲劳试验采用比例与非比例加载路径。
补充资料:卧式单轴、多轴自动半自动操作规程
适用机型:
1、 单轴自动车床:
CG110(1A10?),C1318(1A118),C1325(1A124),
C1336(1A136),A12,A20,A40。
2、 多轴自动、半自动车床:
C24·4(1240·4),C25·4,C2140·P4,C2150·4D,C2132·6D,C2132·6,
C24·6(1240·6),C2150·6D,C2216·6,BSA1/2 -4,1290,ANK135,
ANK155,1261M,1261?,1265·6,1265M·6,1240-0
一、认真执行《金属切削机床通用操作规程》有关规定。
二、认真执行下述有关补充规定:
(一) 工作前认真做到:
1、 检查分配轴及凸轮上的凸轮、撞块应完好无裂纹,安装正确,紧固牢靠。
2、 调正机床时,棒料、毛坯的夹紧,只准用手动不准用机动。
(二) 工作中认真做到:
1、 不准加工弯曲、未经冷拨和未经倒角的棒料。
2、 装料时须将料头对准夹头孔,轻轻击进。棒料长度一般以不超出料管200毫米左右为宜。
3、 四轴自动车床不准在第四工位上装料。六轴自动、半自动车床不准在第六工位上装料。
4、 保险键剪断时,就应查明原因,方准更换新键。
1、 单轴自动车床:
CG110(1A10?),C1318(1A118),C1325(1A124),
C1336(1A136),A12,A20,A40。
2、 多轴自动、半自动车床:
C24·4(1240·4),C25·4,C2140·P4,C2150·4D,C2132·6D,C2132·6,
C24·6(1240·6),C2150·6D,C2216·6,BSA1/2 -4,1290,ANK135,
ANK155,1261M,1261?,1265·6,1265M·6,1240-0
一、认真执行《金属切削机床通用操作规程》有关规定。
二、认真执行下述有关补充规定:
(一) 工作前认真做到:
1、 检查分配轴及凸轮上的凸轮、撞块应完好无裂纹,安装正确,紧固牢靠。
2、 调正机床时,棒料、毛坯的夹紧,只准用手动不准用机动。
(二) 工作中认真做到:
1、 不准加工弯曲、未经冷拨和未经倒角的棒料。
2、 装料时须将料头对准夹头孔,轻轻击进。棒料长度一般以不超出料管200毫米左右为宜。
3、 四轴自动车床不准在第四工位上装料。六轴自动、半自动车床不准在第六工位上装料。
4、 保险键剪断时,就应查明原因,方准更换新键。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。
参考词条