Multiaxial fatigue behavior of superalloy GH4169 was investigated by using the thin tubular multiaxial fatigue specimens under proportional and non-proportional loadings at high temperature.
高温多轴疲劳试验采用比例与非比例加载路径。
2.
Biaxial fatigue behaviors of the Zr-4 alloy under proportional and non-proportional loading with the phase angles of 30°, 60° and 90° were studied.
研究了冷变形Zr-4合金在双轴比例和非比例加载下的循环变形行为,结果表明:当循环应变幅较低时,Zr-4合金表现为循环初始硬化随后饱和的特征;随着应变幅提高,初期硬化后,表现为连续循环软化特征;高应变幅下,初期硬化消失,表现为急剧的循环软化。
3.
The deformation behavior of hydrided zircaloy-4 under tension-torsion proportional loading was investigated using the quantitative metallography and the finite element method(FEM).
采用有限元数值分析方法,模拟了含氢化物Zr-4合金拉-扭双轴比例加载下的变形行为。
3) proportioning device
比例装置
4) Proportional and nonproportional loading
比例加载与非比例加载
5) non-proportional loading
非比例加载
1.
Fatigue fracture characteristics of GH4169 super-alloy under non-proportional loading at high temperature;
GH4169合金高温多轴非比例加载下疲劳断口特征
2.
Investigation of fatigue damage parameters under multi-axial non-proportional loading;
多轴非比例加载条件下疲劳损伤参量的研究
3.
Multiaxial fatigue behavior of superalloy GH4169 was investigated by using the thin tubular multiaxial fatigue specimens under proportional and non-proportional loadings at high temperature.
高温多轴疲劳试验采用比例与非比例加载路径。
6) nonproportional loading
非比例加载
1.
Low cycle fatigue properties of cast aluminum alloys 356 under multi-axial nonproportional loading have been investigated in this paper.
结果表明,合金在循环变形过程中表现为循环硬化特征,循环硬化的程度表现出对非比例加载路径的依赖性;在相同等效应变幅值下,合金的非比例加载低周疲劳寿命小于比例加载,且非比例加载低周疲劳寿命也表现出对非比例加载路径的依赖性;在多轴疲劳寿命预测模型中考虑非比例加载路径对疲劳寿命的影响可以大大提高寿命模型预测的精确度。
2.
Based on the micromechanism of multiaxial low cycle fatigue under nonproportional loading of 316L stainless steel,maxium shear strain and nonproportionality of strain paths are considered as damage parameters of low cycle fatigue.
利用对 316L不锈钢多轴非比例加载低周疲劳的试验结果 ,对现有的多轴低周疲劳寿命估算方法进行了讨论 ,基于 316L不锈钢非比例加载低周疲劳的微观机理 ,选择最大剪应变以及应变路径的非比例度作为损伤参量 ,建立了基于临界面方法的新的非比例加载低周疲劳寿命估算公式 ,利用新的非比例加载低周疲劳寿命估算公式对寿命的预测结果表明 :新的寿命估算公式对剪切型破坏的 316L与 316LN不锈钢及拉伸型破坏的 30 4不锈钢非比例加载低周疲劳寿命预言能力比现有的临界面方法精确 。
3.
The case of nonproportional loading and the plastic dissipation of neartip field is discussed in this paper.
本文采用拟全量理论，分析了裂尖区的非比例加载情况，并从理论上导出不同屈服程度下塑性能密度Ｗ，场的统一表达式，有限元场分析证实了此表达式的正确性。
补充资料：载人机动装置
能载送航天员在太空自由飞行的个体装备。最初航天员靠系在身上的安全带走出载人飞船、航天站或航天飞机到舱外，活动范围受到较大限制。为改变这种被动状况，人们研制出飞行自如的载人机动装置。载人机动装置外形象一个背包，由压缩氮气箱、供气系统、喷气推进器、电子控制设备、温度控制装置和蓄电池等组成。它供给航天员呼吸用氧，有维持人体所需温度、湿度等生命保障条件，还装有使航天员与航天器保持?谕还斓郎系淖派璞浮Ｔ厝嘶爸靡愿哐沟魑е鼗肪诚碌姆尚卸Α：教煸辈僮葑笥一凳直凵系氖挚仄骺刂聘哐沟影沧霸诓煌课坏耐平绻芘绯觯愿谋浞尚械乃俣取⒎较蚝妥颂迪稚舷隆⒆笥液颓昂笠贫锏剿匙蚰孀然康摹；爸米坝辛教谆ノ阜莸牡浜凸┢低常乐狗⑸收衔＜昂教煸卑踩?1984年2月7日，美国"挑战者"号航天飞机的航天员B.麦坎德利斯和R.斯图尔特在 285公里高的飞行轨道上第一次不系安全带,驾载人机动装置以10厘米/秒速度进入太空，飞离航天飞机最远距离达90多米，成为航天史上第一批"人体地球卫星"。