1) steel slag containing high vanadium
高钒钢渣
1.
This paper outlined in detail the domestic and foreign technological development on the metallurgy of vanadium extracting, and elaborated the feasibility and significance of withdrawing the vanadium from the steel slag containing high vanadium which is produced by the molten iron contained the vanadium in Panzhihua Iron & Steel Co.
本论文较详细地概述了国内外钒提取冶金的技术发展现状，阐述了攀钢用含钒铁水炼钢产生的高钒钢渣提取钒的可行性及重要意义，并对高钒钢渣熔融还原开展的一系列研究工作进行了全面的总结。
2) converter slag containing vanadium and titanium oxides
钒钛钢渣
3) vanadium-bearing steel slag
含钒钢渣
1.
Process and development prospects of hydrometallurgical vanadium extraction from vanadium-bearing steel slag
浅析含钒钢渣湿法提钒生产工艺与发展前景
4) vanadium slag from steel making
炼钢钒渣
5) Vanadium rich slag
高钒炉渣
6) slag with vanadium and titanium oxides
含钒钛钢渣
补充资料：钒磷铁矿提钒
钒磷铁矿提钒
extraction of vanadium from the bear vanadium phosphosiderite
和94％。fantintiekuang tifan钒磷铁矿提钒(extraetion of vanadium frombear vanadium phosphosiderite)以含钒磷铁矿为原料制取五氧化二钒的帆提取方法。主要包括钠化焙烧和湿法漫出两道作业。直接用作提饥原料的是含饥磷铁。 含钒磷铁是饥磷铁矿电炉生产单质磷和磷肥的副产品。钒磷铁矿分布在美国爱达荷、蒙大拿、怀俄明、犹他等州，含Pz05 24%~32%、V:O。0.267%~0.625%和少量的铬、镍和钥等。美国克尔麦吉(Kerr-MeGee)化学公司所用的含钒磷铁含饥3.26%~5 .2%、磷24.7%~26.6%、铁59.9%一68.5%、铬3.4%一5.7%、镍。.84%~1%。先将含钒磷铁磨至粒度小于。.42mm，配入1.4倍纯碱和。.1倍的食盐在回转窑中于1043~lo63K温度下焙烧，钒便转变成水溶性的钠盐。熔烧块在加热到沸腾的水中浸出，钒、铬、磷均溶入浸出液。浸出浆液经过滤处理。滤液冷却结晶析出磷酸钠晶体，用离心机分离。晶体中如仍含有钒和铬，可用水重溶后再结晶分离，直到获得合格的磷酸钠(NaaPO;)晶体产品。若Na3PO‘结晶母液含磷高于0. 989/L时则要加入CaclZ，使其生成磷酸钙沉淀，然后水解回收钒。随后往母液中加入硝酸铅，沉淀出铬酸铅。此工艺的钒、铬和磷的回收率分别为85%、65%