1) side internal crack of casting billets
铸坯边内裂
2) crack of billet
铸坯内部裂纹
1.
Conformation,inclusions and organization of A36 layered cut-side sample have been ana-lyzed with XL-30 SEM and EDS, The results show that the crack of billet which create from inclusions, especially oxide and silicate, are mostly responsible for the layered cut-side sample.
利用XL-30扫描电镜能谱仪对A36钢板切边分层缺陷的形貌、夹杂物和组织进行分析研究,指出铸 坯内部的氧化物和硅酸盐夹杂引起的铸坯内部裂纹是造成钢板切边分层的主要原因。
3) Slab crack
铸坯裂纹
1.
The reasons of slab crack under unsteady casting were analysed.
分析了非稳态浇注时导致铸坯裂纹产生的原因,通过采取相应的控制措施,降低了非稳态浇注时铸坯裂纹的发生率。
5) Internal cracks in slab
板坯内裂
6) internal tearing
内裂(铸疵)