1) co-irradiated graft copolymerization
共辐照接枝
1.
The experiment proved that co-irradiated graft copolymerization can raise the two performances of high fiber,and the pre-irradiated graft copolymerization can raise adhesion strength only,but to heat-resistant it had no obvious effect.
实验证明,共辐照接枝法可同时提高纤维的两种性能,预辐照接枝则只能提高纤维的粘接性能,对提高其耐热性能无明显作用。
2) Preirradiation graft copolymerization
预辐照接枝共聚
3) peroxidation preirradiation grafting copolymerization
预辐照共聚接枝
4) radiation inarch-copolymerize
辐照接枝共聚
5) radiation grafting
辐照接枝
1.
Acrylic acid (AA) and sodium styrene sulfonate (SSS) were grafted onto highdensity polyethylene film by radiation grafting method, Thus a ion exchange membrane including strong acid and weak acid groups was prepared.
采用辐照接枝的方法,在高密度聚乙烯(HDPE)上接枝丙烯酸(AA)和对苯乙烯磺酸钠(SSS),从而制备出了一种含羧酸基团和磺酸基团的阳离子交换膜。
补充资料：共辐射接枝
分子式：
CAS号：
性质：将作为骨架链(基材)的聚合物A与作为支链的乙烯基单体B置于同一体系中，保持直接接触情况下进行辐照，发生如下接枝共聚反应。此即共辐射接枝。优点是辐照与接枝一步完成，操作简便、易行，聚合物辐解生成的自由基的利用效率高，另外大部分单体B可作为聚合物A的保护剂。缺点是必然发生单体的均聚反应，降低了接枝率，增加了去除均聚物的步骤。
CAS号：
性质：将作为骨架链(基材)的聚合物A与作为支链的乙烯基单体B置于同一体系中，保持直接接触情况下进行辐照，发生如下接枝共聚反应。此即共辐射接枝。优点是辐照与接枝一步完成，操作简便、易行，聚合物辐解生成的自由基的利用效率高，另外大部分单体B可作为聚合物A的保护剂。缺点是必然发生单体的均聚反应，降低了接枝率，增加了去除均聚物的步骤。