1) preradiation grafting
预辐照接枝聚合
2) Preirradiation graft copolymerization
预辐照接枝共聚
3) peroxidation preirradiation grafting copolymerization
预辐照共聚接枝
4) pre-irradiation grafting
预辐照接枝
1.
Polystyrene-divinylbenze-acrylonitrile(SDBAN)resin was synthesized by γ pre-irradiation grafting reaction and mutual radiation graftin reaction with acry lonitrile.
苯环有共轭π结构,它的π电子是非定域的,辐射时苯基吸收的能量虽然足以使键断裂,但由于能量很快在整个分子重新分布,把能量集中于某一键使其断裂几率是很低的,所以采用预辐照接枝法所需的吸收剂量很大,相关的研究报道很少。
2.
A study was carried out on the preparation of cation-exchange membranes using a one-step method obtained by pre-irradiation grafting of acrylic acid (AA) and sodium styrene sulfonate (SSS) onto high-density polyethylene (HDPE).
高密度聚乙烯预辐照接枝丙烯酸和对苯乙烯磺酸钠单体混合溶液,运用一步法制备了一种羧酸基团和磺酸基团共存的阳离子交换膜,并考察了单体总浓度、辐照剂量、反应温度及交联剂用量诸因素对接枝率的影响规律,找到了实验条件与接枝率的对应关系。
5) radiation inarch-copolymerize
辐照接枝共聚
6) radiation grafting
辐照接枝
1.
Acrylic acid (AA) and sodium styrene sulfonate (SSS) were grafted onto highdensity polyethylene film by radiation grafting method, Thus a ion exchange membrane including strong acid and weak acid groups was prepared.
采用辐照接枝的方法,在高密度聚乙烯(HDPE)上接枝丙烯酸(AA)和对苯乙烯磺酸钠(SSS),从而制备出了一种含羧酸基团和磺酸基团的阳离子交换膜。
补充资料：预辐射接枝
分子式：
CAS号：
性质：将聚合物A在有氧或真空下进行辐照，然后将辐照过的聚合物A浸入单体B中进行接枝反应。优点是：辐照与接枝分步进行，接枝单体不直接接受辐射能，因此最大限度地减少了射线引发了均聚反应；由于辐照与接枝是两个独立的过程，因此即使研究单位和生产单位没有辐照装置和相应的专业人员，也可用该方法进行生产和研究。缺点是聚合物自由基的利用效率较低。
CAS号：
性质：将聚合物A在有氧或真空下进行辐照，然后将辐照过的聚合物A浸入单体B中进行接枝反应。优点是：辐照与接枝分步进行，接枝单体不直接接受辐射能，因此最大限度地减少了射线引发了均聚反应；由于辐照与接枝是两个独立的过程，因此即使研究单位和生产单位没有辐照装置和相应的专业人员，也可用该方法进行生产和研究。缺点是聚合物自由基的利用效率较低。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。