1) pre-irradiation grafting
预辐照接枝
1.
Polystyrene-divinylbenze-acrylonitrile(SDBAN)resin was synthesized by γ pre-irradiation grafting reaction and mutual radiation graftin reaction with acry lonitrile.
苯环有共轭π结构,它的π电子是非定域的,辐射时苯基吸收的能量虽然足以使键断裂,但由于能量很快在整个分子重新分布,把能量集中于某一键使其断裂几率是很低的,所以采用预辐照接枝法所需的吸收剂量很大,相关的研究报道很少。
2.
A study was carried out on the preparation of cation-exchange membranes using a one-step method obtained by pre-irradiation grafting of acrylic acid (AA) and sodium styrene sulfonate (SSS) onto high-density polyethylene (HDPE).
高密度聚乙烯预辐照接枝丙烯酸和对苯乙烯磺酸钠单体混合溶液,运用一步法制备了一种羧酸基团和磺酸基团共存的阳离子交换膜,并考察了单体总浓度、辐照剂量、反应温度及交联剂用量诸因素对接枝率的影响规律,找到了实验条件与接枝率的对应关系。
2) preradiation grafting
预辐照接枝聚合
3) Preirradiation graft copolymerization
预辐照接枝共聚
4) peroxidation preirradiation grafting copolymerization
预辐照共聚接枝
5) radiation grafting
辐照接枝
1.
Acrylic acid (AA) and sodium styrene sulfonate (SSS) were grafted onto highdensity polyethylene film by radiation grafting method, Thus a ion exchange membrane including strong acid and weak acid groups was prepared.
采用辐照接枝的方法,在高密度聚乙烯(HDPE)上接枝丙烯酸(AA)和对苯乙烯磺酸钠(SSS),从而制备出了一种含羧酸基团和磺酸基团的阳离子交换膜。
补充资料：预辐射接枝
分子式：
CAS号：
性质：将聚合物A在有氧或真空下进行辐照，然后将辐照过的聚合物A浸入单体B中进行接枝反应。优点是：辐照与接枝分步进行，接枝单体不直接接受辐射能，因此最大限度地减少了射线引发了均聚反应；由于辐照与接枝是两个独立的过程，因此即使研究单位和生产单位没有辐照装置和相应的专业人员，也可用该方法进行生产和研究。缺点是聚合物自由基的利用效率较低。
CAS号：
性质：将聚合物A在有氧或真空下进行辐照，然后将辐照过的聚合物A浸入单体B中进行接枝反应。优点是：辐照与接枝分步进行，接枝单体不直接接受辐射能，因此最大限度地减少了射线引发了均聚反应；由于辐照与接枝是两个独立的过程，因此即使研究单位和生产单位没有辐照装置和相应的专业人员，也可用该方法进行生产和研究。缺点是聚合物自由基的利用效率较低。