2) UV-irradiation grafting
紫外光辐射接枝
3) UV-induced graft
紫外照射接枝
1.
PE films pretreated by Ar plasma were subjected to UV-induced graft polymerization with acrylamide without photo-initiator.
利用等离子体技术和紫外照射接枝相结合在聚乙烯膜表面接枝丙烯酰胺(AAm)以改善其亲水性。
4) radiation grafting
辐照接枝
1.
Acrylic acid (AA) and sodium styrene sulfonate (SSS) were grafted onto highdensity polyethylene film by radiation grafting method, Thus a ion exchange membrane including strong acid and weak acid groups was prepared.
采用辐照接枝的方法,在高密度聚乙烯(HDPE)上接枝丙烯酸(AA)和对苯乙烯磺酸钠(SSS),从而制备出了一种含羧酸基团和磺酸基团的阳离子交换膜。
6) irradiation grafting
辐照接枝
1.
Study on modification of polyvinylidene fluoride ultrafiltration membranes by Co 60 irradiation grafting;
聚偏氟乙烯超滤膜的辐照接枝改性研究
2.
To modify the surface of nanoSiO2, polytyrene and polyethylacrylate were grafted onto the particles through irradiation grafting polymerization, respectively.
分别用苯乙烯和丙烯酸乙酯对纳米SiO2进行辐照接枝聚合改性,通过两步熔融共混工艺与聚丙烯(PP)共混制备了SiO2/PP复合材料。
补充资料：辐射接枝
分子式：
CAS号：
性质：利用高能射线如x射线、γ射线、电子束、微波等对聚合物进行辐射，使之产生大分子自由基并进一步与其他单体接枝共聚的一种技术。低能射线如紫外线也可用于表面接枝，如在难于染色的聚合物表面接枝甲基丙烯酸甲酯或乙烯基吡啶等进行改善；在疏水聚合物表面接枝含亲水基团(如-COOH或-OH)的单体使聚合物具有亲水性，则能使之抗静电。辐射接枝法有两种：共存接枝法、用射线辐射聚合物A与单体B的混合物得到接枝聚合物；预辐射法，首先辐射聚合物A，接着用单体B处理，从而得到接枝聚合物。
CAS号：
性质：利用高能射线如x射线、γ射线、电子束、微波等对聚合物进行辐射，使之产生大分子自由基并进一步与其他单体接枝共聚的一种技术。低能射线如紫外线也可用于表面接枝，如在难于染色的聚合物表面接枝甲基丙烯酸甲酯或乙烯基吡啶等进行改善；在疏水聚合物表面接枝含亲水基团(如-COOH或-OH)的单体使聚合物具有亲水性，则能使之抗静电。辐射接枝法有两种：共存接枝法、用射线辐射聚合物A与单体B的混合物得到接枝聚合物；预辐射法，首先辐射聚合物A，接着用单体B处理，从而得到接枝聚合物。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。