1) Cr/CrNx multilayer films
Cr/CrNx多层膜
2) Ni/Cr multilayer film
Ni/Cr多层膜
1.
Ni/Cr multilayer film was prepared by the way of Ne+ ion beam mixing.
用Ne离子束混合法制备了Ni／Cr多层膜，用Auger光电子能谱（AES）、X射线衍射（XRD）分析离子束混合多层膜的元素组成、分布和相结构，将其结果与简单蒸发沉积的Ni／Cr多层膜结构进行比较同时，对多层膜（轰击与未轰击）的硬度及摩擦学性能进行测定分析比较结果表明，离子束混合多层膜的硬度和抗磨性能与简单蒸发沉积多层膜相比都有提高这主要是因为Ne离子的轰击作用使多层膜更加致密及膜内的碳化铬硬质弥散相向界面处偏聚，使多层界面的强化作用得到加强，从而提高了多层膜的抗磨性
3) Cr/CrN multilayers
Cr/CrN多层薄膜
1.
The columnar grain growth in CrN film can not be observed in Cr/CrN multilayers,and the crystalline orientation of the multilayers is different from CrN film.
利用射频磁控溅射制备了Cr/CrN多层薄膜,并对比单层CrN薄膜,分析研究了多层膜周期与结构和性能之间的关系。
4) (Ti,Cr)N film
(Ti,Cr)N多元膜层
5) Co/Cr/Pd multilayers
Co/Cr/Pd多层膜
1.
The influences of two measurement procedures on the magnetic properties of Co/Cr/Pd multilayers with different Cr layer thickness were studied.
研究了测量程序对不同Cr层厚度的Co/Cr/Pd多层膜磁性的影响 ,分析了反磁化机理在不同测量程序中对磁性准确性的影响。
6) CrNX films
CrNX薄膜
1.
CrNX films on 45# steel substrate were deposited using multi-arc ion plating technique.
采用电弧离子镀技术在45#钢衬底表面沉积了CrNX薄膜。
补充资料：全氟羧酸-磺酸多层阳离子交换膜
分子式：
CAS号：
性质：又称全氟羧酸-磺酸多层阳离子交换膜，需在膜的一面形成一羧酸膜层。其制法是将全氟磺酸膜片与全氟羧酸膜片加热层压而成，或在全氟磺酸膜的一面经化学处理，使—SO3H转换成—COOH基。这种离子膜一面为—SO3H基，另一面为—COOH，用聚四氟乙烯织物增强，在氯化钠电解制碱中的电流效率为95%左右。
CAS号：
性质：又称全氟羧酸-磺酸多层阳离子交换膜，需在膜的一面形成一羧酸膜层。其制法是将全氟磺酸膜片与全氟羧酸膜片加热层压而成，或在全氟磺酸膜的一面经化学处理，使—SO3H转换成—COOH基。这种离子膜一面为—SO3H基，另一面为—COOH，用聚四氟乙烯织物增强，在氯化钠电解制碱中的电流效率为95%左右。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条