1) FePt Multilayers
FePt多层膜
2) FePt/C multilayer
FePt/C多层膜
1.
The highest coercivity of FePt/C multilayers annealed at 550℃ was obtained when the total thickness of the multilayers was about 30 nm.
因此可以通过控制周期数得到具有合适的微观结构和高的磁学性能的FePt/C多层膜,从而满足超高密度磁记录介质的要求。
3) FePt/Cu multilayer
FePt/Cu多层膜
1.
FePt/Cu multilayers and FePt thin films were prepared by DC magnetron sputtering.
采用直流磁控溅射方法制备FePt/Cu多层膜,再经不同温度下真空热处理得到有序L10-(FePt)100-xCux薄膜。
4) BN/FePt multilayer films
BN/FePt多层膜
5) FePt/Ag doublerlayer films
FePt/Ag双层膜
6) FePt films
FePt薄膜
1.
Effects of annealing with high magnetic fields on the structure and magnetic properties of FePt films
强磁场退火对FePt薄膜结构与磁性能的影响
2.
In this paper, the recent researches in FePt films field are introduced in detail, the mechanisms of reducing the ordering temperature, keeping grain size, decreasing the exchange interaction, controlling the easy axis orientation .
详细介绍了FePt薄膜近年来的研究成果,分析了降低FePt有序化温度,减小FePt颗粒的粒径,减弱晶粒间相互作用和控制其易磁化轴取向的方法,并对其应用前景作了分析。
3.
Chemically self-assembled FePt films were rapidly annealed at different temperatures.
将化学自组装法制备的FePt薄膜进行快速退火,利用X射线衍射仪和振动样品磁强计对薄膜的结构和磁性进行了研究。
补充资料：全氟羧酸-磺酸多层阳离子交换膜
分子式：
CAS号：
性质：又称全氟羧酸-磺酸多层阳离子交换膜，需在膜的一面形成一羧酸膜层。其制法是将全氟磺酸膜片与全氟羧酸膜片加热层压而成，或在全氟磺酸膜的一面经化学处理，使—SO3H转换成—COOH基。这种离子膜一面为—SO3H基，另一面为—COOH，用聚四氟乙烯织物增强，在氯化钠电解制碱中的电流效率为95%左右。
CAS号：
性质：又称全氟羧酸-磺酸多层阳离子交换膜，需在膜的一面形成一羧酸膜层。其制法是将全氟磺酸膜片与全氟羧酸膜片加热层压而成，或在全氟磺酸膜的一面经化学处理，使—SO3H转换成—COOH基。这种离子膜一面为—SO3H基，另一面为—COOH，用聚四氟乙烯织物增强，在氯化钠电解制碱中的电流效率为95%左右。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条