1) open-tube cycling-temperature annealing
开管变温循环热处理
2) high temperature thermomechanical cycle treatment
高温形变循环热处理
1.
3at%Ni alloy was studied by high temperature thermomechanical cycle treatment using Gleeble-3800 thermal simulator system of American Dynamic System Inc.
3at%Ni合金进行高温形变循环热处理,研究不同热处理工艺对其组织细化的影响。
3) cyclical phase transformation treatment
循环相变热处理
4) cyclic heat treatment
循环热处理
1.
Refining single-step canned forging microstructure of Ti-46Al-8.5b-0.2W alloy by cyclic heat treatment process;
循环热处理细化一次锻造的Ti-46Al-8.5Nb-0.2W合金组织
2.
Grain refinement of Ti-46Al-2Nb-2Cr alloy by cyclic heat treatment;
用循环热处理细化Ti-46Al-2Nb-2Cr合金的显微组织
3.
The influence of cyclic heat treatment on the life of punching and shearing dies made of carbon tool steel T8A was studied.
对碳素工具钢T8A采用循环热处理晶粒超细化后对冲裁模具寿命的影响进行了试验研究。
5) circle heat treatment
循环热处理
1.
Fein full lamellar (FFL) microstructure could be obtained by the method of circle heat treatment in (α+γ)phase field.
经验证明均匀的细晶粒双态复相组织γ TiAl基合金具有较好的加工性能 ,常用的获得这种组织的热处理工艺是通过在α+γ相区循环热处理获得的。
6) thermal cycling
循环热处理
1.
Under thermal cycling treatment, the chang of Vickers-Hardness(HV) and phase in iron-based superalloyis studied by TEM, et al.
借助透射电镜等手段,研究了循环加热状态下,铁基高温合金的维氏硬度变化及相交过程,结果表明,实验合金在57℃到650℃之间循环热处理,固溶处理后再经循环热处理的试样的硬度随循环次数的增加而增加;固溶处理加两次时效处理后再经热循环的试样,循环次数少于30次时,硬度随循环次数的增加而减小,循环加热次数多于30次,硬度随循环次数的增加而增加,其硬度的变化与合金中析出的有序相的尺寸及分布有关。