1) W/Ni alloy
W/Ni合金
2) Ni-W alloy
Ni-W合金
1.
Study on mechanical properties of Ni-W alloy films in micro-electro-mechanical system
MEMS中Ni-W合金薄膜力学性能的研究
2.
The Ni-W alloy plates were prepared by electro-deposition on copper substrate using nickel sulphate and sodium tungstate as precursors.
以硫酸镍及钨酸钠为主盐,采用电沉积法在Cu基体上制得了Ni-W合金镀层。
3.
Decorative Ni-W alloy deposits alternative to chromium was prepared by electroplating in citric acid solution.
在柠檬酸溶液体系中,通过电沉积制备出了Ni-W合金装饰性代铬镀层。
3) Ni–W alloy
Ni–W合金
4) W-Ni-Fe alloy
W-Ni-Fe合金
1.
Warm compacting behavior of W-Ni-Fe alloy with different lubricant contents;
润滑剂含量不同时W-Ni-Fe合金的温压行为
5) Ni-W(D) alloy
Ni-W(D)合金
6) W-Fe-Ni alloy
W-Fe-Ni合金
1.
The machining experiment was made on W-Fe-Ni alloy by orthogonal test method.
采用极差分析法分析基于正交试验的W-Fe-Ni合金车削试验结果。
2.
The experiment was carried out on W-Fe-Ni alloy semi-sphere parts by using orthogonal test method to study the turned surface roughness, and results of experiments were analyzed by using maximum difference method.
运用正交试验法对W-Fe-Ni合金半球试件车削加工表面粗糙度进行了试验,并采用极差分析法分析了试验结果。
补充资料：Ni3Al基金属间化合物高温合金
Ni3Al基金属间化合物高温合金
Ni_(3)Al-base intermetallic compound superalloy
N一3AIJ一J旧shuJ一an huahewu goowen heJ一nNi3AI基金属间化合物高温合金(Ni3AI一baseintermetallie eompound superalloy)以Ni3AI相为基体的金属间化合物高温合金。Ni3AI作为高温合金材料中的强化相口)早已被人们所熟知。单晶Ni3AI有较好的室温塑性和加工性，但多晶Ni3AI在室温的塑性儿乎为零。1979年，日本和泉修等发现，添加微量硼可使Ni3AI韧化。硼强烈地偏聚于晶界，从而提高晶界的结合强度并使晶界区无序化，因此提高了晶界区塑性变形能力，使Ni3AI的室温拉伸伸长率可达50%以上。纯净N珠AI的室温、高温强度偏低，与高温合金相比需要进一步提高。固溶强化(见高温合金固溶强化)是提高强度的一条有效途径。Ni3AI可以固溶很多元素，其中以错和铅的强化效果最显著。美国橡树岭国家试验室已发展了一系列含铬、错、错等元素的Ni3AI基金属间化合物高温合金，具有良好的强度、塑性和高温抗氧化性。中国也对Ni3AI基合金进行了深入研究，并添加微量镁显著改善了热加工塑性。Ni3AI基合金可能是最先在工业上得到使用的金属间化合物高温合金之一，已制成各种部件在试用，如汽轮机和柴油机的耐热部件、高温模具、加热元件以及航空用的紧固件等。 〔邹敦叙)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条