1) W-Mo-Ni-Fe alloy
W-Mo-Ni-Fe合金
1.
A method determining W, Mo, Ni and Fe contents at the same time for W-Mo-Ni-Fe alloy by using energy diffuse X-ray fluorescence (EDXRF) spectroscopy is described.
介绍了用能量色散X射线荧光光谱法(EDXRF)同时测定W-Mo-Ni-Fe合金组分的分析方法。
2) Ni-Cr-Fe-Mo-Co-W Alloy
Ni-Cr-Fe-Mo-Co-W合金
3) W-Mo-Fe alloys
W-Mo-Fe 合金
4) Fe-Ni-Mo alloys
Fe-Ni-Mo合金
1.
Fe-Ni-Mo alloys were electrodeposited from acid citrate-chloride electrolyte.
在酸性柠檬酸盐-氯化物电解液中电沉积制备Fe-Ni-Mo合金,通过SEM、XRD及XPS对合金表面形貌、微观结构及表面化学状态进行分析,结果表明:合金镀层表面平整,结构致密,无孔洞及裂纹;Fe-Ni-Mo合金属于纳米晶,面心立方结构,呈现较强的(111)晶面择优取向;Mo原子是以取代原子的方式进入FeNi固溶体,形成置换固溶体。
5) W-Ni-Fe alloy
W-Ni-Fe合金
1.
Warm compacting behavior of W-Ni-Fe alloy with different lubricant contents;
润滑剂含量不同时W-Ni-Fe合金的温压行为
6) W-Fe-Ni alloy
W-Fe-Ni合金
1.
The machining experiment was made on W-Fe-Ni alloy by orthogonal test method.
采用极差分析法分析基于正交试验的W-Fe-Ni合金车削试验结果。
2.
The experiment was carried out on W-Fe-Ni alloy semi-sphere parts by using orthogonal test method to study the turned surface roughness, and results of experiments were analyzed by using maximum difference method.
运用正交试验法对W-Fe-Ni合金半球试件车削加工表面粗糙度进行了试验,并采用极差分析法分析了试验结果。
补充资料：W-Ni-Fe alloy
分子式：
CAS号：
性质：一类重要的钨基重合金。它们是在钨中添加镍、铁而组成的合金，以及在这个基础上再加入其他金属元素的合金。加入的镍铁比一般为7：3或1：1。这类合金应用极广，已经成为用量最大的主要钨基重合金。其特点是烧结密度高，强度与塑性均较好，有一定的铁磁性。合金作为一般应用，如配重、平衡锤、防辐射屏蔽装置等，都直接使用烧结合金；但如作为要求高机械性能的应用时，合金则需变形加工及热处理以达到强化。
CAS号：
性质：一类重要的钨基重合金。它们是在钨中添加镍、铁而组成的合金，以及在这个基础上再加入其他金属元素的合金。加入的镍铁比一般为7：3或1：1。这类合金应用极广，已经成为用量最大的主要钨基重合金。其特点是烧结密度高，强度与塑性均较好，有一定的铁磁性。合金作为一般应用，如配重、平衡锤、防辐射屏蔽装置等，都直接使用烧结合金；但如作为要求高机械性能的应用时，合金则需变形加工及热处理以达到强化。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。