1) FePt/AIN thin film
FePt/AlN薄膜
2) FePt films
FePt薄膜
1.
Effects of annealing with high magnetic fields on the structure and magnetic properties of FePt films
强磁场退火对FePt薄膜结构与磁性能的影响
2.
In this paper, the recent researches in FePt films field are introduced in detail, the mechanisms of reducing the ordering temperature, keeping grain size, decreasing the exchange interaction, controlling the easy axis orientation .
详细介绍了FePt薄膜近年来的研究成果,分析了降低FePt有序化温度,减小FePt颗粒的粒径,减弱晶粒间相互作用和控制其易磁化轴取向的方法,并对其应用前景作了分析。
3.
Chemically self-assembled FePt films were rapidly annealed at different temperatures.
将化学自组装法制备的FePt薄膜进行快速退火,利用X射线衍射仪和振动样品磁强计对薄膜的结构和磁性进行了研究。
3) FePt(001)film
FePt(001)薄膜
4) FePt thin films
FePt薄膜
1.
Magnetic and magneto-optical properties of perpendicularly c-axis orientated FePt thin films;
c轴垂直取向FePt薄膜的磁和磁光性能研究
2.
The influence of the Ag substrate on the structure and magnetic properties of FePt thin films;
Ag衬底层对FePt薄膜结构和性能的影响
3.
FePt thin films are potential candidates for ultrahigh density magnetic recording media since L1_0 ordered FePt crystals have a high magnetocrystalline anisotropy energy density.
具有L1_0有序结构的FePt薄膜由于具有很高的磁晶各向异性常数而成为新一代超高密度磁记录介质材料。
6) FePt series thin films
FePt基薄膜
补充资料：aluminium nitride material AlN
分子式：
CAS号：
性质： 该材料有陶瓷型和薄膜型两种。氮化铝热导率高、绝缘性能好，电阻率高达4×106Ω·cm。热膨胀系数小(2.65～3.80)×10-6K-1，化学性能稳定，在1000℃时才与空气发生氧化。在真空中可稳定到1500℃。致密型氮化铝是抗水的，几乎不与浓无机酸发生反应。密度为3.26g/cm3，熔点2400℃，弹性模量为300～310GPa，抗弯强度为280～350MPa，莫氏硬度为8。A1N陶瓷用粉末冶金法制得。氮化铝薄膜用反应溅射法制得。A1N陶瓷片用于大功率半导体集成电路和大功率的厚膜电路，A1N薄膜用于薄膜器件的介质和耐磨、耐热、散热好的材料表面镀层。
CAS号：
性质： 该材料有陶瓷型和薄膜型两种。氮化铝热导率高、绝缘性能好，电阻率高达4×106Ω·cm。热膨胀系数小(2.65～3.80)×10-6K-1，化学性能稳定，在1000℃时才与空气发生氧化。在真空中可稳定到1500℃。致密型氮化铝是抗水的，几乎不与浓无机酸发生反应。密度为3.26g/cm3，熔点2400℃，弹性模量为300～310GPa，抗弯强度为280～350MPa，莫氏硬度为8。A1N陶瓷用粉末冶金法制得。氮化铝薄膜用反应溅射法制得。A1N陶瓷片用于大功率半导体集成电路和大功率的厚膜电路，A1N薄膜用于薄膜器件的介质和耐磨、耐热、散热好的材料表面镀层。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条