1) shaping ability
成形能力
1.
Comparative study of shaping ability between rotary ProTaper and Flexofile;
机用ProTaper锉和Flexofile不锈钢锉根管成形能力的对比研究
2) glass-forming ability
形成能力
1.
We studied the glass-forming ability and mechanical properties of Mg-Cu-Ni-Nd alloy system.
对Mg-Ni-Cu-Nd系列合金的非晶形成能力与力学性能进行了研究,发现四元合金Mg62。
2.
By considering mechanical properties and the effect on glass-forming ability (GFA) of choosing elements, glass-forming alloys were designed based on Mg-Cu-Nd, Mg-Ni-Cu-RE (RE=Y, Nd), Mg-Zn-Ca and Mg-Ni-Zn-Y, respectively.
本文通过合金元素的力学特性和对Mg基非晶形成能力的分析,确定了以Mg-Cu-Nd、Mg-Ni-Cu-RE(RE=Y,Nd)、Mg-Zn-Ca和Mg-Ni-Zn-Y合金为主要研究对象,通过铜模铸造方法制备了不同直径的圆柱样品。
3) forming ability
形成能力
1.
The glass forming ability and the thermal stability were also investigated by differential scanning calorimetry(DSC)and X-Ray diffraction(XRD).
利用XRD和DSC等手段对该合金的形成能力及热稳定性进行了分析。
2.
The influence of microstructure and technological conditions on glass-forming ability(GFA)of bulk metallic glasses are briefly analyzed.
回顾了大块金属玻璃的研究和进展过程,介绍了典型及新型大块金属玻璃及其开发年代,简要分析了微观结构以及工艺条件对大块金属玻璃的形成能力的影响,介绍了大块金属玻璃优良的力学、磁学性能,特别介绍了大块金属玻璃的可焊性及广阔的应用前景。
4) glass forming ability
非晶形成能力
1.
Effects of Zr on glass forming ability and thermal stability of alloy system Al-Ni-Y-Zr-Cu;
Zr对Al-Ni-Y-(Zr,Cu)合金系非晶形成能力及热稳定性的影响
2.
Effects of additional element on the glass forming ability and corrosion resistance of bulk Zr-based amorphous alloys;
Zr基大块非晶中添加元素对非晶形成能力及耐蚀性的影响
3.
Effect of Cu on glass forming ability and mechanical properties of Mg-Zn-Ca alloys
Cu对Mg-Zn-Ca合金非晶形成能力与力学性能的影响
5) glass forming ability
玻璃形成能力
1.
Prediction of glass forming ability using atomic radius and electro-negativity;
以原子半径和电负性预测玻璃形成能力
2.
Effect of Nd on glass forming ability of bulk amorphous M g-Cu-Y-Nd alloys;
Nd对块体Mg-Cu-Y-Nd非晶合金玻璃形成能力的影响
3.
Influence of zirconium on microstructure and glass forming ability of Co-based alloy;
Zr对Co基合金铸态组织和玻璃形成能力的影响
6) glass-forming ability
玻璃形成能力
1.
Analysis of glass-forming ability and properties of amorphous alloys Co_(48)Cr_(15)Mo_(14)C_(15)B_6Re_2 (Re=Y or Gd);
Co_(48)Cr_(15)Mo_(14)C_(15)B_6Re_2(Re=Y,Gd)非晶合金的玻璃形成能力及性能分析
2.
Correlations between viscosity and glass-forming ability in bulk amorphous alloys
块体非晶合金的黏度与玻璃形成能力的关系
3.
Criteria of glass-forming ability based on characteristic temperatures
基于特征温度的玻璃形成能力判据
补充资料：主要射出成形材料成形时应注意事项
■主要射出成形材料成形时应注意事项
品 名 注 意 事 项
PVC
聚氯乙烯
1. 产品种类范围非常广（硬质、软质、聚合物等），成型条件各有不同，从熔融至分
解之温度范围很小，尤须注意加热温度。
2. 附着水分少，但成型周期尽可能减少（50℃~60℃热风干燥）。
3. 成型机方面，与材料直接接触的部位须电镀或采用不锈钢以防热分解所产生的盐酸
侵蚀。射出压力2100kg/cm2程度。
4. 所有塑料当中必须是细心注意温度调节。
5. 浇口附近易产生流纹，故射出操作后，柱塞不要后退使浇口充分固化后再瞬间退后为宜。
6. 加热之初温不宜高，特别注意熔融情形。第二级加热温度较高，且尽可能使成形周
期缩短，比较安全。
PA
聚醯胺树脂
1. 成型温度比其它材料高，故采用油加热的成形机较适当。
2. 吸湿性大，必须充分干燥。水分对成型品的品质影响甚大（80℃热风干燥约5~6小时）。
3. 须退火以消除内部歪斜。
PP
聚丙烯
1. 同PE，但成形温度必须较高。熔融温度170℃，超过190℃则流动性大增，则毛边增加，
易产生接缝及凹入情形。
PC
聚碳酸脂
1. 吸湿性比尼龙小，但若有些微之水分存在则成型品产生其它色泽或气泡，故必须密封
干燥同时成形时也须预备干燥（120℃之温度4小时）。
2. 加热温度超过320℃时则产生热分解，成品变色，故特别注意温度调节，又成型时的温度调节也非常重要，须特别注意其最低温度、最低时间。
3. 须退火以消除内部歪斜（130℃~135℃，1小时程度为准）。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。