1) high temperature quenching and tempering
高温淬火回火
2) high temperature quenching
高温淬火
1.
The effect of heat treatment crafts, common quenching, high temperature quenching, sub-zero treatment after quenching and so on,on strengthening and toughing properties of cold-punched mould steel was studied.
对 60Si2Mn冷冲模具钢采用常规淬火、高温淬火及淬火后深冷处理等热处理工艺进行强韧化对比试验,结果表明,经常规淬火深冷处理后其强韧性远超过高温淬火工艺,是一种实用性很强的强韧化工艺。
2.
Surface heat treatment,and high temperature quenching could extend the die life.
提出采用表面渗碳或碳氮共渗、高温淬火热处理工艺,能使热作模具使用寿命大幅提高。
3.
The effect of high temperature quenching followed by tempering on microscopic structures and mechanical properties of 3Cr2W8V steel has been studied by using X Ray Diffraction and Transmission Electron Microscope (TEM).
利用Ｘ射线衍射和透射电子显微镜（ＴＥＭ）研究了３Ｃｒ２Ｗ８Ｖ钢高温淬火后回火对显微组织和力学性能的影响，着重讨论了回火转变与冲击韧度的关系。
3) Quenching-Tempering Temperature
淬-回火温度
1.
Effect of Quenching-Tempering Temperature on Structure and Properties of High Strength Steel 30NCD16;
淬-回火温度对高强度钢30NCD16组织和性能的影响
4) Quench-tempering temperature
淬火-回火温度
5) super high temperature quenching
超高温淬火
1.
With the aid of TEM,the effect of multi stepped tempering at high temperature on the microstructure and mechanical properties of the 46CrNiMoVA steel after super high temperature quenching has been investigated.
本文借助透射电镜初步探讨了多次高温回火处理对４６ Ｃｒ Ｎｉ Ｍｏ Ｖ Ａ 钢超高温淬火后的微观组织与力学性能的影响。
6) quenching and tempering
淬火回火
1.
The development and current application situation as well as achievements of heat treatment equipment in annealing,quenching and tempering,carburization and induction heating of bearing parts at home and abroad were discussed.
论述了国内外轴承零件退火、淬火回火、渗碳和感应加热等热处理装备的开发、应用现状和成果 ,提出了国内轴承热处理装备技术水平与工业发达国家之间的差距以及国内外轴承热处理装备今后的发展趋