2) amide-imide
酰胺酰亚胺
1.
Then, poly(ester-amide-imide) polyols were prepared via melt-copolycondensation of AIDA-Ⅰ or AIDA-Ⅱ, adipic acid, neopentyl glycol, and glycerol.
以偏苯三酸酐、甲苯二异氰酸酯及间/对苯二甲酸(m/p-PTA)合成的酰胺酰亚胺二元酸(AIDA- 或AIDA- ),与己二酸、新戊二醇及甘油熔融共缩聚得到酰胺酰亚胺聚酯多元醇,采用该多元醇与封闭型多异氰酸酯经高温脱封交联后成功地制得一种交联型酰胺酰亚胺聚氨酯膜。
3) polyamideimide
聚酰胺亚胺
1.
s:\ A head to head,end to end structural polyamideimide(PAI)baking paint was synthesized from the reaction of dimaleopimaric acid with di isocyanates,and modified by means of copolymerization with dihydric alcohol to prepare poly(urethane amideimide)(PUAI)baking paint.
采用双马来海松酸酰亚胺和二苯基甲烷二异氰酸酯制备头 头 ,尾 尾结构的聚酰胺亚胺 (PAI)烘漆 ,并与二元醇共聚 ,制备聚 (氨酯 酰胺亚胺 ) (PUAI)烘漆 ,进一步改善漆膜的各项力学性能。
4) aminimide
胺基酰亚胺
1.
The main development directions of aminimide compounds synthesized by unsymmertrical dimethyl-hydrazine(UDMH) during the past decade were reviewed.
回顾了国外近十年来关于利用偏二甲肼(UDMH)合成胺基酰亚胺(aminimide或aminemide)化合物的研究进展。
2.
Aiming at the problem of recycling scraps unsymmetrical dimethylhydrzine(UDMH),eight saturated aliphatic aminimides with low melting points were synthesized after UDMH was alkylated,acidylated and dehydrogenated.
为了解决报废偏二甲肼再利用问题,使偏二甲肼经烷基化、酰基化、脱氢,合成了八种具有较低熔点的饱和脂肪族胺基酰亚胺化合物。
5) polyaminobismaleimide
聚胺-酰亚胺
6) aminimide
胺化酰亚胺
补充资料：1,8-萘内酰亚胺
分子式：C11H7NO
分子量：169.19
CAS号：130-00-7
性质：细针状结晶，熔点180-181℃。易溶于沸水，微溶于乙醚。
制备方法：用1,8-萘二甲酰亚胺重排而得。在反应锅内加水，氢氧化钠溶液及苛性钾溶液，边搅拌边加入次氯酸钠及扩散剂NNO，在30℃时加1,8-萘二甲酰亚胺，在28-30℃保温2.5h。在反应过程中保持次氯酸钠过量。保温结束，以重亚硫酸钠消除过量的次氯酸钠，以盐酸调整为9.5-10。滤去未反应的萘二酰亚胺，滤液在40℃以下，以盐酸酸析至pH为2-3。加热至80-85℃，保温半小时，闭环。冷却至60℃，过滤、洗涤，得1,8-萘内酰亚胺。
用途：染料中间体。
分子量：169.19
CAS号：130-00-7
性质：细针状结晶，熔点180-181℃。易溶于沸水，微溶于乙醚。
制备方法：用1,8-萘二甲酰亚胺重排而得。在反应锅内加水，氢氧化钠溶液及苛性钾溶液，边搅拌边加入次氯酸钠及扩散剂NNO，在30℃时加1,8-萘二甲酰亚胺，在28-30℃保温2.5h。在反应过程中保持次氯酸钠过量。保温结束，以重亚硫酸钠消除过量的次氯酸钠，以盐酸调整为9.5-10。滤去未反应的萘二酰亚胺，滤液在40℃以下，以盐酸酸析至pH为2-3。加热至80-85℃，保温半小时，闭环。冷却至60℃，过滤、洗涤，得1,8-萘内酰亚胺。
用途：染料中间体。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。