1) nickel-boronizing
镍-硼共渗
1.
Formation mechanism of surface layer structure in nickel-boronizing steel was studied using metallography,X-Ray diffraction,SEM and WDS technique.
本文运用金相、扫描电镜波谱仪以及X射线衍射技术和残余应力测试研究分析了碳钢的镍-硼共渗层组织结构、形成机理及性能特点。
2) nickel-plating and boronizing
镀镍渗硼
1.
This paper analyses the structure and properties of nickel-plating and boronizing layer.
分析研究了镀镍渗硼层组织结构和性能特点。
3) boronsiliconizing
硼硅共渗
1.
The influences of aluminosiliconizing and boronsiliconizing on the microstructure and oxidation resistance of the coatings were researched.
用粉末固体渗法在钼合金表面制备了MoSi2渗层,研究了铝硅共渗和硼硅共渗对渗层的结构和抗氧化性能的影响。
4) Boron-aluminizing
硼铝共渗
1.
Study on the Self-protective Boron-aluminizing Paste;
自保护硼铝共渗膏剂研究
5) borovanadizing
硼钒共渗
1.
The results show that borovanadizing layer is more thick and more compact than that of boronizing layer.
采用光学显微镜、扫描电镜和电子探针等检测手段,分析了20钢固体法渗硼和硼钒共渗的渗层组织结构、成分特点及其硬度分布。
6) boron-vanadizing
硼钡共渗
补充资料：碳氮硼三元共渗
分子式：
CAS号：
性质：碳氮硼三元共渗是使钢制工件同时渗入碳、氮、硼三种元素的化学热处理工艺。共渗后渗层的硬度较渗硼为低(HV600～1000)。碳氮硼三元共渗如用于石油机械易损零件，能提高使用寿命。碳氮硼三元共渗后空冷即可得到HV750的硬度，对于上述钢材制造的薄小工件，可以省去淬火工序。碳氮硼三元共渗也可以在气体介质中进行，例如用尿素(2500g)、甲醇(8L)、硼酸三甲酯(5L)、丙酮(6L)的混合渗剂滴入840~860℃的井式渗碳炉中，保温3～5h后，在低碳合金渗碳钢上可得到0.4～0.6mm渗层，表面硬度达HRC63～65，甚至更高。
CAS号：
性质：碳氮硼三元共渗是使钢制工件同时渗入碳、氮、硼三种元素的化学热处理工艺。共渗后渗层的硬度较渗硼为低(HV600～1000)。碳氮硼三元共渗如用于石油机械易损零件，能提高使用寿命。碳氮硼三元共渗后空冷即可得到HV750的硬度，对于上述钢材制造的薄小工件，可以省去淬火工序。碳氮硼三元共渗也可以在气体介质中进行，例如用尿素(2500g)、甲醇(8L)、硼酸三甲酯(5L)、丙酮(6L)的混合渗剂滴入840~860℃的井式渗碳炉中，保温3～5h后，在低碳合金渗碳钢上可得到0.4～0.6mm渗层，表面硬度达HRC63～65，甚至更高。