1) boronitriding
硼氮共渗
1.
Study on improving the hot forging dies service life of 5CrMnMo Steel of boronitriding;
硼氮共渗提高5CrMnMo钢热锻模使用寿命的研究
2.
Research for the Structures, Properties and the Mechanism of Borosulphurizing and Boronitriding;
硼硫、硼氮共渗组织和性能及其机理的研究
3.
Microstructure of the boronitriding layer on austenitic stainless steel and the transition zone between the layer and matrix has been examined.
研究了奥氏体不锈钢硼氮共渗渗层及过渡区组织结构,并对共渗机理进行了探讨。
2) N-B co-penetration
氮硼共渗
1.
Study on binary N-B co-penetration character of No.45 steel in lower temperature condition;
针对目前渗硼存在温度高、脆性大等一系列问题,对45钢进行气体低温氮硼共渗得到复合渗层,并对渗层进行金相组织观察、显微硬度测试,探讨了渗层的形成过程及渗剂中催渗剂尿素的作用。
3) silicoboronitriding
硅硼氮共渗
4) Re-B-C-N multi-element penetration
稀土硼碳氮共渗
1.
RE-B-C-N multi-element penetration of 65Mn steel metal rubber with larger wire diameter
大丝径65Mn金属橡胶稀土硼碳氮共渗
5) boronitriding adding RE
加稀土硼氮共渗
6) pack boronitriding
固体硼氮共渗
1.
The boronitriding medium,process paramaters,microstructures and properties of case,application on dies of pack boronitriding are studied in this paper.
研究了固体硼氮共渗技术的渗剂、工艺参数、共渗后的组织与性能及其在模具上的应用。
补充资料：碳氮硼三元共渗
分子式：
CAS号：
性质：碳氮硼三元共渗是使钢制工件同时渗入碳、氮、硼三种元素的化学热处理工艺。共渗后渗层的硬度较渗硼为低(HV600～1000)。碳氮硼三元共渗如用于石油机械易损零件，能提高使用寿命。碳氮硼三元共渗后空冷即可得到HV750的硬度，对于上述钢材制造的薄小工件，可以省去淬火工序。碳氮硼三元共渗也可以在气体介质中进行，例如用尿素(2500g)、甲醇(8L)、硼酸三甲酯(5L)、丙酮(6L)的混合渗剂滴入840~860℃的井式渗碳炉中，保温3～5h后，在低碳合金渗碳钢上可得到0.4～0.6mm渗层，表面硬度达HRC63～65，甚至更高。
CAS号：
性质：碳氮硼三元共渗是使钢制工件同时渗入碳、氮、硼三种元素的化学热处理工艺。共渗后渗层的硬度较渗硼为低(HV600～1000)。碳氮硼三元共渗如用于石油机械易损零件，能提高使用寿命。碳氮硼三元共渗后空冷即可得到HV750的硬度，对于上述钢材制造的薄小工件，可以省去淬火工序。碳氮硼三元共渗也可以在气体介质中进行，例如用尿素(2500g)、甲醇(8L)、硼酸三甲酯(5L)、丙酮(6L)的混合渗剂滴入840~860℃的井式渗碳炉中，保温3～5h后，在低碳合金渗碳钢上可得到0.4～0.6mm渗层，表面硬度达HRC63～65，甚至更高。