1) Double-roller casting
双辊式铸轧
2) 2 high continuous casting mill
双辊式连续铸轧
3) twin roll casting
双辊铸轧
1.
But for twin roll casting alloy,the microstructure changed from dendrite to fibrous deformation structure after several passes hot rolling at 350℃.
轧制后两种合金均具有良好的力学性能,双辊铸轧合金的强度和延伸率均明显高于传统铸造合金的强度和延伸率,两种合金1 mm厚薄带经350℃/10 min均匀化退火后的抗拉强度、屈服强度和延伸率分别为334。
2.
In order to improve the forming property of twin roll casting magnesium alloy sheets AZ31B, homogenizing treatment was carried out at different annealing temperature (300,350,400℃) and the holding time (1,2,3 h).
为提高双辊铸轧AZ31B镁合金薄板的成形性能,在不同退火温度(300、350、400℃)和保温时间(1、2、3h)下对铸轧AZ31B镁合金薄板进行均匀化退火试验。
3.
The influence of heating temperature in annealing treatment on morphology of eutectic carbide in twin roll casting strip of high speed steel was studied.
研究了退火加热温度对高速钢双辊铸轧薄带中共晶碳化物形态的影响·试验结果表明 ,随着加热温度的提高 ,铸轧薄带中的网状共晶碳化物陆续熔断 ,粒状碳化物逐渐增多·当加热温度达到 95 0℃后 ,铸轧薄带中的网状共晶碳化物基本上被粒状碳化物所取代·用汤普森 弗瑞锥其 (Thompson Friedrich)方程 ,对试验结果进行了分析 ,并得出共晶碳化物层片间距的减小为高速钢铸轧薄带中的共晶碳化物的熔断和球化提供了条件
4) twin-roll casting
双辊铸轧
1.
Microstructure of Twin-roll Casting Magnesium Alloy Strip;
双辊铸轧镁合金板坯微观组织特征
2.
The study of new technology on producing wrought magnesium alloy thin strip by twin-roll casting;
双辊铸轧法生产变形镁合金薄带新工艺的研究
3.
Modelling of solidification microstructure evolution of twin-roll casting magnesium strip using cellular automaton
用元胞自动机方法模拟镁合金薄带双辊铸轧过程凝固组织
5) twin-roll strip casting
双辊铸轧
1.
Grain refinement of high-speed steel on twin-roll strip casting;
双辊铸轧高速钢薄带的晶粒细化
2.
Establishment of process data acquisition system of twin-roll strip casting and results analysis;
双辊铸轧薄带钢工艺参数检测系统的建立与结果分析
3.
Finite element numerical simulation on the temperature fields of the twin-roll strip casting;
双辊铸轧薄带钢温度场的有限元数值模拟
6) twin roll strip casting
双辊铸轧
1.
The possibility of manufacturing weathering steel strips by twin roll strip casting was explored.
由此可见,采用双辊铸轧生产方式不仅可以抑制钢中有害元素如磷和铜的偏析,同时还提高材料的力学性能,起到变废为宝的作用。
2.
Based on the existing condition of the lab, a mathematical model for the twin roll strip casting is presented.
针对实验室现有的实验设备条件,建立了双辊铸轧薄带钢过程的有限元数学模型,通过程序开发对熔池内的温度场进行了模拟;给出了各工艺参数对凝固终点位置及铸带表面温度的影响规律,为铸轧过程的分析和控制提供了理论依据。
3.
Experimental study on the twin roll strip casting of stainless steel was carried out using laboratory unequal diameter twin roll caster at state key laboratory of rolling and automation, Northeastern University.
在异径双辊铸轧机上进行了不锈钢薄带铸轧的实验研究 ,掌握了诸如浇注温度、铸轧速度、铸轧压力、预留辊缝的大小等薄带钢铸轧的合理工艺参数 ,成功地铸轧了不锈钢带卷 ;对铸轧薄带的显微组织进行分析 ,并比较了晶粒细化的效果 ;依据铸轧实验研究的结果 ,分析了影响工艺稳定性的主要因素 ,得到了工艺稳定性方面的深层规律
补充资料：双辊式机头口型挤出
分子式：
CAS号：
性质：双辊式机头口型即宽幅口型,主要用于挤出胶板或胶片,可挤压出厚2～20mm、宽2.5m的胶板或胶片。代替三辊或四辊压延机挤出输送带覆盖胶及衬里胶片等。双辊式机头口型由扁平机头和小型两辊压延机组成。胶料从扁平口型挤出约30～60mm厚的胶板,然后进入两辊压延机压成所需厚度的胶片。优点是压制胶片厚度大于3mm也不会产生气泡。
CAS号：
性质：双辊式机头口型即宽幅口型,主要用于挤出胶板或胶片,可挤压出厚2～20mm、宽2.5m的胶板或胶片。代替三辊或四辊压延机挤出输送带覆盖胶及衬里胶片等。双辊式机头口型由扁平机头和小型两辊压延机组成。胶料从扁平口型挤出约30～60mm厚的胶板,然后进入两辊压延机压成所需厚度的胶片。优点是压制胶片厚度大于3mm也不会产生气泡。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条