1) Corundum-mullite block(CMB)
刚玉莫来石砖
2) Mullite bonded corundum brick
莫来石结合刚玉砖
3) Corhart block , Corhart Standard
电熔莫来石-刚玉耐火砖
4) corundum-mullite materials
刚玉-莫来石
1.
The effect of NaF on the synthesis of corundum-mullite materials from high aluminum fly ash;
NaF对高铝粉煤灰合成刚玉-莫来石材料的影响
2.
In this paper,the influence of temperature and Li2O on the properties,crystal structure,and morphology of corundum-mullite materials prepared from fly ash and bauxite was studied.
研究了Li2O、烧结温度对高铝粉煤灰和铝矾土合成刚玉-莫来石材料的性能、物相组成和显微结构的影响。
5) corundum-mullite
刚玉莫来石
1.
Effects of micro-powder and firing temperature on microstructure and properties of corundum-mullite materials;
微粉及烧成温度对刚玉莫来石材料结构的影响
6) mullite-corundum
莫来石-刚玉
1.
Lightweight mullite-corundum materials were prepared by a gel-casting method,using bauxite,silica fume and polystyrene ball as starting materials.
以高铝矾土、硅灰、聚苯乙烯球作原料,用凝胶注模工艺制备高强轻质莫来石-刚玉材料,确定最佳pH值和分散剂用量,并研究了烧成后样品的强度、气孔率、热导率、物相组成和微观结构。
补充资料：莫来石砖
分子式：
CAS号：
性质：以莫来石（3Al2O3·2SiO2）为主晶相的高铝质耐火材料。一般氧化铝含量在65%～75%之间。矿物组成除莫来石外，其中含氧化铝较低者还含有少量玻璃相和方石英；含氧化铝较高者还含有少量刚玉。耐火度较高，可达1790℃以上。荷重软化开始温度1600～1700℃。常温耐压强度70～260MPa。抗热震性良好。有烧结莫来石砖和电熔莫来石砖两种。烧结莫来石砖以高铝矾土熟料为主要原料，加入少量黏土或生矾土作结合剂，经成型、烧成而制成。电熔莫来石砖以高矾土、工业氧化铝和耐火黏土为原料，加入木炭或焦炭细粒作还原剂，成型后采用还原电熔法来制造。电熔莫来石的结晶比烧结莫来石大，抗热震性比烧结制品好。他们的高温性能主要取决于氧化铝的含量和莫来石相与玻璃分布的均匀性。主要用于热风炉炉顶、高炉炉身和炉底、玻璃熔窑蓄热室、陶瓷烧结窑、石油裂解系统死角炉衬等。
CAS号：
性质：以莫来石（3Al2O3·2SiO2）为主晶相的高铝质耐火材料。一般氧化铝含量在65%～75%之间。矿物组成除莫来石外，其中含氧化铝较低者还含有少量玻璃相和方石英；含氧化铝较高者还含有少量刚玉。耐火度较高，可达1790℃以上。荷重软化开始温度1600～1700℃。常温耐压强度70～260MPa。抗热震性良好。有烧结莫来石砖和电熔莫来石砖两种。烧结莫来石砖以高铝矾土熟料为主要原料，加入少量黏土或生矾土作结合剂，经成型、烧成而制成。电熔莫来石砖以高矾土、工业氧化铝和耐火黏土为原料，加入木炭或焦炭细粒作还原剂，成型后采用还原电熔法来制造。电熔莫来石的结晶比烧结莫来石大，抗热震性比烧结制品好。他们的高温性能主要取决于氧化铝的含量和莫来石相与玻璃分布的均匀性。主要用于热风炉炉顶、高炉炉身和炉底、玻璃熔窑蓄热室、陶瓷烧结窑、石油裂解系统死角炉衬等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。