1) corundum/mollite
刚玉-莫来石相
1.
The experimental results show that the microstructure of the new ceramic tile can be improved by mending the present formula,decreasing the percentage of voids and increasing the corundum/mollite,and that the bulk density,compr.
实验研究结果表明,通过优化现有陶瓷墙地砖的工艺配方,改善陶瓷墙地砖微观结构,有利于降低陶瓷墙地砖的气孔率,提高陶瓷墙地砖的致密度和刚玉-莫来石相含量,可获得导热系数为2。
2) mullite-corundum phase
莫来石-刚玉相
3) corundum-mullite materials
刚玉-莫来石
1.
The effect of NaF on the synthesis of corundum-mullite materials from high aluminum fly ash;
NaF对高铝粉煤灰合成刚玉-莫来石材料的影响
2.
In this paper,the influence of temperature and Li2O on the properties,crystal structure,and morphology of corundum-mullite materials prepared from fly ash and bauxite was studied.
研究了Li2O、烧结温度对高铝粉煤灰和铝矾土合成刚玉-莫来石材料的性能、物相组成和显微结构的影响。
4) corundum-mullite
刚玉莫来石
1.
Effects of micro-powder and firing temperature on microstructure and properties of corundum-mullite materials;
微粉及烧成温度对刚玉莫来石材料结构的影响
5) mullite-corundum
莫来石-刚玉
1.
Lightweight mullite-corundum materials were prepared by a gel-casting method,using bauxite,silica fume and polystyrene ball as starting materials.
以高铝矾土、硅灰、聚苯乙烯球作原料,用凝胶注模工艺制备高强轻质莫来石-刚玉材料,确定最佳pH值和分散剂用量,并研究了烧成后样品的强度、气孔率、热导率、物相组成和微观结构。
6) corundum-mullite composites
刚玉-莫来石复相材料
补充资料：莫来石陶瓷
分子式：
CAS号：
性质：以莫来石（3Al2O3·2SiO2）为主晶相的陶瓷。莫来石属斜方晶系。密度为3.23g/cm3。熔点在1810℃左右。介电系数为7。硬度为6～7。原料粒度愈细，烧结温度愈低，抗弯强度愈高。其成型方法取决于制品的形状及坯料的性质，如干压、热压铸、车坯、注浆或等静压等。莫来石瓷属液相烧结，烧成存在两大问题：一是体积有变化，可通过预烧来消除；二是烧成温度范围窄，约20～30℃，故需严格控制烧成温度，使用温度均匀的窑炉来煅烧。
CAS号：
性质：以莫来石（3Al2O3·2SiO2）为主晶相的陶瓷。莫来石属斜方晶系。密度为3.23g/cm3。熔点在1810℃左右。介电系数为7。硬度为6～7。原料粒度愈细，烧结温度愈低，抗弯强度愈高。其成型方法取决于制品的形状及坯料的性质，如干压、热压铸、车坯、注浆或等静压等。莫来石瓷属液相烧结，烧成存在两大问题：一是体积有变化，可通过预烧来消除；二是烧成温度范围窄，约20～30℃，故需严格控制烧成温度，使用温度均匀的窑炉来煅烧。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。