1)  Crystal transformation
晶转
2)  crystal transformation
结晶转变
1.
The results showed that the thermal expansion coefficients of PTFE composites in the crystal transformation temperature zone are about 3 to 5 times on their average values in the whole analyze zone.
结果表明,PTFE基复合材料在结晶转变区内的线膨胀系数可达到平均值的3~5倍。
3)  isomorphous transformation
同晶转化
4)  monotectic transition
偏晶转变
1.
Bi is added into high silica Al-alloy to form multicomponent Al-Si Bi whose crystallization has the character of monotectic transition.
高硅铝合金中加入Bi形成Al-Si-Bi多元合金,具有偏晶转变的结晶特点。
2.
Adding element Bi to eutectic crystal and hyper-eutectic Al-Si alloy and forming multiple unit Al-Si-Bi alloy, whose crystallization typify the monotectic transition.
共晶、过共晶Al-Si合金中加入元素Bi形成Al-Si-Bi多元合金,具有偏晶转变的结晶特点,由于Bi的不溶性及自润滑性,并以高弥散游离态兮布干基体中使过共晶Al-Si合金的耐磨性大幅度提高。
5)  crystallization conversion
结晶转化
6)  eutectic transformation
共晶转变
1.
Solidifying structures and eutectic transformation form of alumina/zinc alloy composites;
氧化铝/锌合金复合材料的凝固组织及其共晶转变模式
参考词条
补充资料：多晶转变
分子式：
CAS号：

性质：又称多晶转变。同种物质由于环境温度变化，材料中晶体结构发生相应变化的现象。晶型转变的温度称为转变点，也即相变点。晶型转变可分为可逆和不可逆转变两大类。还有快速转变(即位移型)和慢速转变(即断键重组型)之分。由于不同晶型比重不同，内部质点排列不同，因此晶型转变时伴有体积变化、导电率变化和比热容变化等现象发生，对材料生产工艺和使用有重要影响。例如β石英←→α石英在573℃时发生快速转变，而石英、鳞石英和方石英之间的转变属慢转变。又如ZrO2单斜←→四方之间的转变在1170℃时快速进行，并伴有显著体积变化，加热时收缩，冷却时膨胀，两种晶型可反复瞬时转变，利用多晶转变现象产生的微裂纹可达到增加陶瓷材料韧性之目的。