1) cellular to dendritic transition
胞-枝晶转变
2) cell/dendrite transition
胞/枝晶转变
1.
The simulation results show that during cell/dendrite transition the mixed structure is composed of cells and dendrites,in which the secondary dendrites are absent at facing surface of some parallel closely spaced dendrites.
采用基于溶质扩散控制模型CA方法对Ti44Al合金定向凝固初始阶段变速冷却过程中胞/枝晶转变过程进行了数值模拟。
3) cellular dendritic transition
胞枝晶转变
4) transition from dendrite to fine cell
枝晶→细胞晶转变
1.
From the stability of the cylindrical interface, a criterion of the transition from dendrite to fine cell in sub-rapid solidification has been constructed.
关键词##4亚快速凝固;;枝晶→细胞晶转变;;柱形界面稳定
5) dendrite to cellular transition
枝晶/胞晶转变
6) cell-to-dendrite transition
胞枝转变
1.
The typical cell-to-dendrite transition is observed at the center of laser melt pool, and a detailed investigation on the transition conditions shows that the critical transition velocity determined by experiment agrees well w.
在激光熔池中观察到典型的胞枝转变，对转变的临界条件进行了深入研究，结果表明：实验确定的胞枝转变临界速度与最近提出的ＢＪＴ模型的预言值符合得较好。
补充资料：多晶转变
分子式：
CAS号：
性质：又称多晶转变。同种物质由于环境温度变化，材料中晶体结构发生相应变化的现象。晶型转变的温度称为转变点，也即相变点。晶型转变可分为可逆和不可逆转变两大类。还有快速转变(即位移型)和慢速转变(即断键重组型)之分。由于不同晶型比重不同，内部质点排列不同，因此晶型转变时伴有体积变化、导电率变化和比热容变化等现象发生，对材料生产工艺和使用有重要影响。例如β石英←→α石英在573℃时发生快速转变，而石英、鳞石英和方石英之间的转变属慢转变。又如ZrO2单斜←→四方之间的转变在1170℃时快速进行，并伴有显著体积变化，加热时收缩，冷却时膨胀，两种晶型可反复瞬时转变，利用多晶转变现象产生的微裂纹可达到增加陶瓷材料韧性之目的。
CAS号：
性质：又称多晶转变。同种物质由于环境温度变化，材料中晶体结构发生相应变化的现象。晶型转变的温度称为转变点，也即相变点。晶型转变可分为可逆和不可逆转变两大类。还有快速转变(即位移型)和慢速转变(即断键重组型)之分。由于不同晶型比重不同，内部质点排列不同，因此晶型转变时伴有体积变化、导电率变化和比热容变化等现象发生，对材料生产工艺和使用有重要影响。例如β石英←→α石英在573℃时发生快速转变，而石英、鳞石英和方石英之间的转变属慢转变。又如ZrO2单斜←→四方之间的转变在1170℃时快速进行，并伴有显著体积变化，加热时收缩，冷却时膨胀，两种晶型可反复瞬时转变，利用多晶转变现象产生的微裂纹可达到增加陶瓷材料韧性之目的。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。