1) Mullite bonded corundum brick
莫来石结合刚玉砖
2) Corundum-mullite block(CMB)
刚玉莫来石砖
3) Corhart block , Corhart Standard
电熔莫来石-刚玉耐火砖
4) corundum-mullite materials
刚玉-莫来石
1.
The effect of NaF on the synthesis of corundum-mullite materials from high aluminum fly ash;
NaF对高铝粉煤灰合成刚玉-莫来石材料的影响
2.
In this paper,the influence of temperature and Li2O on the properties,crystal structure,and morphology of corundum-mullite materials prepared from fly ash and bauxite was studied.
研究了Li2O、烧结温度对高铝粉煤灰和铝矾土合成刚玉-莫来石材料的性能、物相组成和显微结构的影响。
5) corundum-mullite
刚玉莫来石
1.
Effects of micro-powder and firing temperature on microstructure and properties of corundum-mullite materials;
微粉及烧成温度对刚玉莫来石材料结构的影响
6) mullite-corundum
莫来石-刚玉
1.
Lightweight mullite-corundum materials were prepared by a gel-casting method,using bauxite,silica fume and polystyrene ball as starting materials.
以高铝矾土、硅灰、聚苯乙烯球作原料,用凝胶注模工艺制备高强轻质莫来石-刚玉材料,确定最佳pH值和分散剂用量,并研究了烧成后样品的强度、气孔率、热导率、物相组成和微观结构。
补充资料：熔铸莫来石砖
分子式：
CAS号：
性质：又称电熔莫来石砖，俗称铁砖或黑铁砖，矿物组成中主要为莫来石（占60%～70%）的熔铸耐火材料，属弱酸性耐火材料。主要成分氧化铝，含量为65%～75%，二氧化硅含量25%左右，其他氧化物总量为5%～8%。熔铸莫来石砖化比较致密，耐火度为1730～1800℃，荷重软化开始温度为1700℃，高温强度和耐磨性较高，耐侵蚀性较强。热膨胀系数较小。导热系数也较高，因此，耐热震性较其他熔铸砖好。以高铝矾土、工业氧化铝及耐火黏土为原料，经电炉熔化、浇铸、退火而制成。主要用于玻璃熔窑等工业窑炉中。
CAS号：
性质：又称电熔莫来石砖，俗称铁砖或黑铁砖，矿物组成中主要为莫来石（占60%～70%）的熔铸耐火材料，属弱酸性耐火材料。主要成分氧化铝，含量为65%～75%，二氧化硅含量25%左右，其他氧化物总量为5%～8%。熔铸莫来石砖化比较致密，耐火度为1730～1800℃，荷重软化开始温度为1700℃，高温强度和耐磨性较高，耐侵蚀性较强。热膨胀系数较小。导热系数也较高，因此，耐热震性较其他熔铸砖好。以高铝矾土、工业氧化铝及耐火黏土为原料，经电炉熔化、浇铸、退火而制成。主要用于玻璃熔窑等工业窑炉中。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。