1) molting infiltrating Si
熔融渗Si
2) reactive melt infiltrating Si
反应熔渗Si
3) liquid silicon infiltration
熔融渗硅
1.
This paper presents the developments of C/C-SiC composites fabricated by liquid silicon infiltration(LSI),which is an easy operation and low cost process with short periods.
与其它制备工艺相比,采用熔融渗硅法制备 C/C-SiC 复合材料的工艺具有操作简单、周期短、成本低等优点。
2.
Now,C/C-SiC friction composites were fabricated by the combination of chemical vapor infiltration(CVI)with liquid silicon infiltration(LSI),and C/C performs were prepared by densification of needled carbon fiber felts with CVI.
本文以针刺炭纤维整体毡为预制体,采用化学气相渗透法制备C/C多孔体,然后熔融渗硅制得C/C-SiC材料;研究了C/C-SiC材料的组织结构、力学性能及其失效模式、摩擦磨损性能及机理,同时介绍了中南大学研制的C/C-SiC制动材料的应用现状。
4) behavior of liquid infiltration
熔Si浸渗行为
5) spontaneous melt infiltration
自发熔融浸渗
1.
A novel spontaneous melt infiltration methodology was developed for the preparation of phase-change energy storage materials.
研究了融盐Na2SO4与石英质多孔陶瓷预制体的自发熔融浸渗制备工艺,成功地制备出无机盐/陶瓷基(Na2SO4/SiO2)复合相变储能材料,观察和分析了该材料的物相组成与显微结构特征,对该材料的各项热物理性能和机械性能进行了测量。
6) low temperature liquid sulphurization
低温熔融渗硫
1.
Sulfide layers with a certain thickness were made on the surface of Cr12 and 45 steels by means of low temperature liquid sulphurization process.
采用稀土催化低温熔融渗硫新工艺在Cr12钢和45#钢表面获得一定厚度的渗硫层,用X射线衍射仪分析了渗硫层结构;在环-块摩擦磨损试验机上测定了干摩擦条件下渗硫层的摩擦学性能,并利用扫描电子显微镜研究了渗硫层及其磨痕表面形貌。
补充资料：为再结合熔融石英制品、熔融石英陶瓷制品
分子式：
CAS号：
性质：又称为再结合熔融石英制品、熔融石英陶瓷制品或石英玻璃烧结制品。具有良好的化学稳定性。抗酸性和抗冲刷性强。高温机械强度大。热膨胀系数低。气孔率低。导电率低。但在1100℃以上长期使用时，制品中的石英会向方石英转变，使制品产生裂纹和剥落。以熔融石英为原料，经粉碎、成型、干燥、烧成而制得。制法有泥浆浇注法、蜡注法、捣打法、半干压法和等静压成型等。由于在烧成时收缩小，可以制得尺寸精确的制品。可用于制作耐酸容器、反应罐内衬耐酸部件等。冶金工业中用其制成浸入式水口，使用效果很好。