1) liquid phase siliconization
液相渗Si
1.
The high temperature oxidation resistance of the TiAl-based alloy can be obviously improved by liquid phase siliconization through the Al-Si alloy.
使用液相Al-Si合金对TiAl基合金进行表面渗Si处理,可明显增强TiAl基合金的高温抗氧化性,经1273 K,100 h的恒温氧化后,不同的表面涂层使合金在40—100 h之间的氧化速率降低了2个数量级,恒温氧化100 h后的最终氧化皮脱落量也减少3个数量级,液相渗Si使TiAl基合金表面高温抗氧化性能得到大幅度改善,其根本原因是Si与TiAl中的元素Ti结合,降低了Ti的活度,相对增强了涂层中元素Al的活度,而且涂层中Al的绝对含量也得到明显提高,这些均抑制了高温氧化过程中TiO_2的生成,涂层最外层形成了致密的Al_2O_3氧化膜。
2) liquid phsase epitaxy of Si
Si液相处延
3) infiltration
[英][,infil'treiʃən] [美][,ɪnfɪl'treʃən]
液相浸渗
1.
And C/Mg composite is prepared under a low pressure infiltration and the damping property is improved.
该涂层改善了碳纤维与镁合金基体的润湿性,实现了低压液相浸渗制备C/Mg复合材料,并提高了复合材料的阻尼性能。
4) liquid Si infiltration
液相渗硅
5) liquid infiltration
液相渗透
1.
On-line liquid infiltration joining of carbon fiber reinforced silicon carbide (C/SiC) composites was carried out with Ni alloy as the interlayer at the temperature of 1 300℃ a holding time of 45min in vacuum and at an applied pressure of 20MPa.
为得到C/SiC复合材料的强连接,利用三维编织碳纤维增韧碳化硅(C/SiC)复合材料在制备过程中残留的孔隙,采用Ni合金作为中间层在1 300℃保温45min、真空条件下对三维C/SiC复合材料用液相渗透连接方法进行了在线连接,所施压力为20MPa。