1) liquid-vapor infiltration
液气相渗透
2) liquid-vaporised infiltration
液相气化渗透
3) chemical liquid vapour infiltration
化学液气相渗透
1.
The principles and characteristics of the four densification methods for C/C composites were introcuced,including chemical vapour infiltration(CVI),liquid impregnation,CVI+liquid impregnation and chemical liquid vapour infiltration.
综合论述了化学气相渗透(CVI)、液相浸渍、CVI+液相浸渍和化学液气相渗透等4种增密碳纤维增强碳基(C/C)复合材料方法的原理和它们的特点。
4) liquid infiltration
液相渗透
1.
On-line liquid infiltration joining of carbon fiber reinforced silicon carbide (C/SiC) composites was carried out with Ni alloy as the interlayer at the temperature of 1 300℃ a holding time of 45min in vacuum and at an applied pressure of 20MPa.
为得到C/SiC复合材料的强连接,利用三维编织碳纤维增韧碳化硅(C/SiC)复合材料在制备过程中残留的孔隙,采用Ni合金作为中间层在1 300℃保温45min、真空条件下对三维C/SiC复合材料用液相渗透连接方法进行了在线连接,所施压力为20MPa。
6) CLVI
化学液相气化渗透
1.
Chemical Liquid-vaporized Infiltration(CLVI)is at present the most rapid densification process for fabricating Carbon/Carbon composites.
论述了化学液相气化渗透工艺(简称 CLVI)制备 C/C 复合材料的基本原理、工艺特点,分析了该技术的沉积机理、热解碳的形成条件和组织结构与致密化环境之间的关系,以及沉积温度和石墨化温度对材料力学性能的影响,概述了该技术在模拟方面的研究现状,展望了其发展前景并提出了自己的观点。