说明：双击或选中下面任意单词，将显示该词的音标、读音、翻译等；选中中文或多个词，将显示翻译。
|
|
|
1) laser chemical heat treatment
激光化学热处理
2) laser heat treatment
激光热处理
1.
Technology and mechanism of laser heat treatment;
激光热处理活塞环工艺与机理研究
2.
Research and application of the laser heat treatment for cam-shafts of the rare earth magnesium nodular graphite cast iron;
稀土镁球墨铸铁凸轮轴激光热处理的研究与应用
3) laser heat treating parameters
激光热处理参数
4) laser phase transformation treatment
激光相变热处理
1.
The electron beam welding(EBW) of TC4 titanium alloy was processed by CO_2 laser phase transformation treatment,and the effects of assistant gas, laser power and spot diameter,etc.
利用CO2激光相变热处理技术对TC4钛合金电子束焊缝进行了处理,研究了激光功率、光斑直径、辅助气体等激光工艺参数对电子束焊缝残余应力分布的影响。
5) laser surface thermal treatment
激光表面热处理
1.
Application of laser surface thermal treatment technology in tubing processing;
激光表面热处理技术在油管加工中的应用
2.
In order to solve the problem of thread gluing of the tubing,Henan Oilfield Machinery Manufacture Factory performs the quenching treatment of tubing and collar surfaces by means of laser surface thermal treatment.
为解决油田现场使用油管时出现的螺纹粘连问题,河南油田机械制造厂利用激光表面热处理技术对油管和接箍表面进行淬火处理。
6) laser heat-treatment machine
激光热处理机
补充资料：一种古老而实用的化学热处理方法
介绍一种古老而实用的化学热处理方法 原苏联资料报道：
每70g苏打粉（Na2HCO3）和亚铁氰化钾（黄白盐）加1kg木屑配制成的固体渗碳剂，均匀混合后即可使用。工艺：930℃×4h，渗层可达1.0mm，要达到此渗速，普通固体渗碳要8h。此法渗速快，成本低，而且节能。
1、 渗碳：
（1）、木屑+5-10%BaCO3制成固体渗碳剂（加催渗剂），820-830℃×1-1.5h，渗层可达0.25-0.30mm，碳浓度达0.70%-0.90%，生产劳动条件优于一般固体渗碳，节电70%，成本仅为原工艺的30%。
（2）、90%木屑+10%Na2CO3制成渗碳剂。
（3）、 88%木屑+12%BaCO3制成渗碳剂。
（4）、 66%木屑+27% BaCO3+7% Na2CO3制成渗碳剂（一般薄辟件不用此法）。
2、固体渗氮：
60%木屑+30%尿素+7%生石灰+3%氯化铵，渗氮温度（550±10℃），时间4-10h，渗层厚0.12-0.15 mm。适用于3Cr2W8V、H13等热作模具，高速钢刀具制品等。
3、C-N共渗
80%木炭+12%木屑+7.5%尿素+0.5-1% Na2CO3组成C、N共渗剂。
4、防氧化保护剂（木屑+3-5% Na2CO3）：
（1） 如：为了节约Cr12MoV合金钢材料，把磨损的模具翻新利用，有较高的经济价值。其工艺：
缩孔加热，780-790℃；高温回火700-720℃；淬火加热980-1000℃时，都撒上木屑适量，能起很好的保护作用。
（2） 工、模具、结构件等在箱式炉中退火时，只要在工件上撒上一层木屑，退火后工件表面光洁美观。
（3） 在高速钢锻件上放一些木屑，再装箱退火，能大大减轻氧化脱碳程度。
（4） 高速钢刀具或模具返修品在空气炉中退火时，能保证工件不氧化、脱碳。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。