1) Plunger speed by cavity filling
充型时的冲头速度
2) Filling Velocity
充型速度
1.
The Influence of Various Process Parameters on the Liquid Metal Filling Velocity in Gray Iron Casting Produced by EPC V Process;
铸铁件EPC-V法工艺因素对充型速度的影响
2.
The result indicats that there are few blowholes,inclusions except misrun in the casting with the filling velocity of 25mm/s,and the casting was formed with some blowholes、inclusions with the filling velocity of 40mm/s,while the casting was form.
研究了薄壁铝合金铸件真空吸铸充型速度对其内部质量的影响,对一种200mm×180mm,壁厚为2。
3.
The metal filling velocity increases with the reduction of pattern density and coating thickness, and the increase of pouring temperature.
研究了模样密度、涂层厚度、浇注温度、真空度等工艺参数对可控气压下镁合金消失模铸造时液态金属的充填形态和充型速度的影响,以及充型速度与充型形态之间的关系。
3) filling speed
充型速度
1.
The filling speed of lost foam cast iron casting was measured by use of an integrated set of experimental equipment and a specially designed computer acquisition system.
研究了负压度、模样密度、浇注温度、金属静压头等工艺因素对消失模铸铁件充型速度的影响规律。
4) mold filling velocity
充型速度
1.
Study on mold filling velocity in AZ91 magnesium alloy LFC process with vacuum;
AZ91镁合金负压消失模铸造充型速度的研究
2.
The influence of processing parameters on the mold filling velocity during investiment casting was investigated by using an integrated system of experimental equipment and a specially designed computer data acquisition device.
用消失模铸造试验装置和计算机数据采集系统研究了工艺因素对充型速度影响的规律。
3.
The mold filling velocity of AI alloy melt in lost foam casting process was investigated by X-ray technology and other method.
充型中期,充型速度增加较快;而充型末期,由于温度降低以及气压升高,充型速度锐减。
5) velocity of high-speed injection stage
快速充型速度
1.
The results show that the surface quality of magnesium alloy die casting improved greatly with the increase of the velocity of high-speed injection stage in a cert.
针对汽车发动机缸盖罩盖零件,采用压力传感器,通过对铸件的表观质量进行评定及铸件密度和抗拉强度的测定,系统研究了镁合金压铸过程中快速充型速度和起速位置对型腔内压力变化和铸件质量的影响。
6) critical plunger speed
临界冲头速度
补充资料：充炭黑充油丁苯橡胶
分子式：
分子量：
CAS号：
性质：同时含有炭黑和油的丁苯橡胶。性能和用途与充炭黑丁苯橡胶和充油丁苯橡胶相似。由冷聚丁苯胶乳与炭黑的水分散液和油乳液经混合、凝聚、洗涤、过滤、干燥等步骤制得。
分子量：
CAS号：
性质：同时含有炭黑和油的丁苯橡胶。性能和用途与充炭黑丁苯橡胶和充油丁苯橡胶相似。由冷聚丁苯胶乳与炭黑的水分散液和油乳液经混合、凝聚、洗涤、过滤、干燥等步骤制得。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条