1) hydroforming
[英]['haidrə,fɔ:miŋ] [美]['haɪdrə,fɔrmɪŋ]
液力成形
1.
Warm hydroforming process of lightweight alloys;
轻合金热态液力成形技术
2.
Using a length of tube as the blank, hydroforming technology of tubular parts promise an extensive prospect to produce a variety of complex hollow components.
管壳零件轴压液力成形以管材为初始坯料，可制造各种复杂的空心零件，具有广阔的应用前景。
3.
This paper presents the principle, advantages and typical application of internal high pressure forming (IHPF), sheet hydroforming, warm hydroforming and shell hydroforming.
介绍了内高压成形、板料液力成形、热态压力成形和壳体液力成形技术原理、优点和典型应用。
2) tube hydroformng
管材液力成形
3) hydro plasticity
液力塑性成形
4) hydraulic forming press
液压成形压力机
5) tube hydro forming
管材内压液力成形
1.
In the process of tube hydro forming,the tube changes its shape under combined internal pressure and axial compressive load.
管材内压液力成形过程中 ,管坯在内压与轴向压力的共同作用下发生变形。
6) hydroforming
[英]['haidrə,fɔ:miŋ] [美]['haɪdrə,fɔrmɪŋ]
液压成形
1.
Finite element simulation for tube hydroforming process and analysis of failure mode;
圆管液压成形过程有限元模拟及失效分析研究
2.
Dynamic analysis and hydroforming mould design for motorcycle oil box;
摩托车油箱液压成形力学分析及模具设计
3.
A new model of sheet metal hydroforming equipment based on a type YX28-400/650C double-action press;
基于YX28-400/650C双动液压机的板材液压成形装备的研制
补充资料：主要射出成形材料成形时应注意事项
■主要射出成形材料成形时应注意事项
品 名 注 意 事 项
PVC
聚氯乙烯
1. 产品种类范围非常广（硬质、软质、聚合物等），成型条件各有不同，从熔融至分
解之温度范围很小，尤须注意加热温度。
2. 附着水分少，但成型周期尽可能减少（50℃~60℃热风干燥）。
3. 成型机方面，与材料直接接触的部位须电镀或采用不锈钢以防热分解所产生的盐酸
侵蚀。射出压力2100kg/cm2程度。
4. 所有塑料当中必须是细心注意温度调节。
5. 浇口附近易产生流纹，故射出操作后，柱塞不要后退使浇口充分固化后再瞬间退后为宜。
6. 加热之初温不宜高，特别注意熔融情形。第二级加热温度较高，且尽可能使成形周
期缩短，比较安全。
PA
聚醯胺树脂
1. 成型温度比其它材料高，故采用油加热的成形机较适当。
2. 吸湿性大，必须充分干燥。水分对成型品的品质影响甚大（80℃热风干燥约5~6小时）。
3. 须退火以消除内部歪斜。
PP
聚丙烯
1. 同PE，但成形温度必须较高。熔融温度170℃，超过190℃则流动性大增，则毛边增加，
易产生接缝及凹入情形。
PC
聚碳酸脂
1. 吸湿性比尼龙小，但若有些微之水分存在则成型品产生其它色泽或气泡，故必须密封
干燥同时成形时也须预备干燥（120℃之温度4小时）。
2. 加热温度超过320℃时则产生热分解，成品变色，故特别注意温度调节，又成型时的温度调节也非常重要，须特别注意其最低温度、最低时间。
3. 须退火以消除内部歪斜（130℃~135℃，1小时程度为准）。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。