2) yttrium borophosphate
硼磷酸钇
1.
Green emitting phosphors of yttrium borophosphate doped with Ce 3+ ,Tb 3+ and Gd 3+ have been prepared by reaction of BPO 4 with rare earth oxides for the first time.
用 BPO4 和稀土氧化物为原料 ,首次合成了铈、铽、钆共激活的硼磷酸钇绿色荧光粉 ,研究了基质中Ce3+ 、Tb3+ 、Gd3+ 的发光以及它们之间的相互作用。
3) yttrium aluminum borate
四硼酸铝钇
1.
Nd3+-doped yttrium aluminum borate (Nd3+:YAl3(BO3)4, Nd:YAB) nano-sized powder was synthesized by a gel combustion method using Al(NO3)3·9H2O, Y(NO3)3·6H2O, C6H8O7·H2O, B2O3 and Nd2O3 as starting materials.
以硝酸盐为原料、柠檬酸为络合剂,采用凝胶–燃烧法成功制备出了掺钕的四硼酸铝钇[Nd3+:YAl3(BO3)4,Nd:YAB]纳米粉体。
4) lithium yttrium tri-borate doped with neodymium
掺钕三硼酸钇锂
5) Neodymium yttrium aluminum borate
四硼酸铝钇钕
6) YCOB
三硼酸氧钙钇
1.
Growth condition for high quality yttrium calcium oxyborate [YCa 4O(BO 3) 3,YCOB] and neodymium doped yttrium calcium oxyborate(Nd∶YCOB) single crystals were reported in details.
本文详细报道了采用熔体提拉法生长高质量三硼酸氧钙钇［ＹＣａ４Ｏ（ＢＯ３）３，ＹＣＯＢ］和掺钕三硼酸氧钙钇［Ｎｄ∶ＹＣａ４Ｏ（ＢＯ３）３，Ｎｄ∶ＹＣＯＢ］的结果。
补充资料：钯钇合金
分子式：
CAS号：
性质：钯基添加钇的二元合金。钇在钯中的最大固溶液为12（at）%，并产生显著的固溶强化效应。有PdY6.6、PdY8和PdY10等合金。PdY6.6、PdY10的透氢速度分别为4.99cm3/(cm2·s)和5.38 cm3/(cm2·s)(纯钯为1.43 cm3/(cm2·s))。采用电弧炉熔炼，铸锭在含50%氢气氛中进行吸氢软化处理，条件为400℃，2h。易于轧制成箔材，并进行真空退火处理。可用作氢气净化材料。
CAS号：
性质：钯基添加钇的二元合金。钇在钯中的最大固溶液为12（at）%，并产生显著的固溶强化效应。有PdY6.6、PdY8和PdY10等合金。PdY6.6、PdY10的透氢速度分别为4.99cm3/(cm2·s)和5.38 cm3/(cm2·s)(纯钯为1.43 cm3/(cm2·s))。采用电弧炉熔炼，铸锭在含50%氢气氛中进行吸氢软化处理，条件为400℃，2h。易于轧制成箔材，并进行真空退火处理。可用作氢气净化材料。