1) Nd:YCOB
掺钕三硼酸氧钙钇
1.
Growth condition for high quality yttrium calcium oxyborate [YCa 4O(BO 3) 3,YCOB] and neodymium doped yttrium calcium oxyborate(Nd∶YCOB) single crystals were reported in details.
本文详细报道了采用熔体提拉法生长高质量三硼酸氧钙钇［ＹＣａ４Ｏ（ＢＯ３）３，ＹＣＯＢ］和掺钕三硼酸氧钙钇［Ｎｄ∶ＹＣａ４Ｏ（ＢＯ３）３，Ｎｄ∶ＹＣＯＢ］的结果。
2) lithium yttrium tri-borate doped with neodymium
掺钕三硼酸钇锂
3) YCOB
三硼酸氧钙钇
1.
Growth condition for high quality yttrium calcium oxyborate [YCa 4O(BO 3) 3,YCOB] and neodymium doped yttrium calcium oxyborate(Nd∶YCOB) single crystals were reported in details.
本文详细报道了采用熔体提拉法生长高质量三硼酸氧钙钇［ＹＣａ４Ｏ（ＢＯ３）３，ＹＣＯＢ］和掺钕三硼酸氧钙钇［Ｎｄ∶ＹＣａ４Ｏ（ＢＯ３）３，Ｎｄ∶ＹＣＯＢ］的结果。
4) neodymium doped gadolinium calcium oxyborate crystal
掺钕硼酸氧钙钆晶体
5) neodymium-doped lanthanum calcium borate
掺钕硼酸钙镧
6) Neodymium yttrium aluminum borate
四硼酸铝钇钕
补充资料：掺钕钒酸钇激光晶体
分子式：Nd:YVO3
CAS号：
性质：四方晶系锆英石结构单晶体。空间群D4h19-I4/amd。密度4.23g/cm3。莫氏硬度5.0。熔点1635～1730℃。热膨胀系数7.3×10-6/℃(⊥c)。热导率5.1W/(m·K)(⊥c)。折射率n0=1.86，ne=1.88。荧光寿命98μs。F2/3-4I11/2。跃迁波长1.064μm。晶体激光阈值低，效率高，受激发截面大(为20×10-19cm2)，吸收线宽。采用提拉法、浮区区熔等法制备。用于制作LD泵浦。
CAS号：
性质：四方晶系锆英石结构单晶体。空间群D4h19-I4/amd。密度4.23g/cm3。莫氏硬度5.0。熔点1635～1730℃。热膨胀系数7.3×10-6/℃(⊥c)。热导率5.1W/(m·K)(⊥c)。折射率n0=1.86，ne=1.88。荧光寿命98μs。F2/3-4I11/2。跃迁波长1.064μm。晶体激光阈值低，效率高，受激发截面大(为20×10-19cm2)，吸收线宽。采用提拉法、浮区区熔等法制备。用于制作LD泵浦。