2) yttrium phosphate-vanadate
钒磷酸钇
3) yttrium orthovanadate
正钒酸钇
4) Yttrium vanadate(YVO_4)
钒酸钇(YVO_4)
5) ytterbium-doped yttrrium vanadate
掺镱钒酸钇
6) YVO 4 crystal
钒酸钇晶体
1.
The XRD experiments showed that the change of the pH results in different width of XRD lines of YVO 4 crystals for which the material were obtained by the same stoichiometric ratio.
用XPS证明钒酸钇晶体颜色加深以及晶体内部存在的包裹体与形成低价钒酸盐有关。
2.
The unpolarized axial and transverse optical absorption spectrum of Ho 3+ ions in YVO 4 crystal are measured, from which the strength of absorption transition oscillator is obtained.
分别测量了室温下光垂直、平行c轴入射时Ho3+ 掺杂钒酸钇晶体的非极化光吸收谱 ,得到Ho3+ 吸收跃迁振子强度的实验值 。
补充资料：掺钕钒酸钇激光晶体
分子式：Nd:YVO3
CAS号：
性质：四方晶系锆英石结构单晶体。空间群D4h19-I4/amd。密度4.23g/cm3。莫氏硬度5.0。熔点1635～1730℃。热膨胀系数7.3×10-6/℃(⊥c)。热导率5.1W/(m·K)(⊥c)。折射率n0=1.86，ne=1.88。荧光寿命98μs。F2/3-4I11/2。跃迁波长1.064μm。晶体激光阈值低，效率高，受激发截面大(为20×10-19cm2)，吸收线宽。采用提拉法、浮区区熔等法制备。用于制作LD泵浦。
CAS号：
性质：四方晶系锆英石结构单晶体。空间群D4h19-I4/amd。密度4.23g/cm3。莫氏硬度5.0。熔点1635～1730℃。热膨胀系数7.3×10-6/℃(⊥c)。热导率5.1W/(m·K)(⊥c)。折射率n0=1.86，ne=1.88。荧光寿命98μs。F2/3-4I11/2。跃迁波长1.064μm。晶体激光阈值低，效率高，受激发截面大(为20×10-19cm2)，吸收线宽。采用提拉法、浮区区熔等法制备。用于制作LD泵浦。