1) carboxylated NBR
羟基丁腈橡胶
2) hydroxyl-terminated nitrile rubber
端羟基丁腈橡胶
1.
The solution copolymerization of butadiene and acrylonitrile for the synthesis of hydroxyl-terminated nitrile rubber was studied with H2O2 as initiator and ethanol as solvent in a l0 L and a 50 L polymerization reactors.
在１０Ｌ和５０Ｌ不锈钢聚合釜中，以合成端羟基丁腈橡胶（ＨＴＢＮ）为目的，用Ｈ＿２Ｏ＿２作引发剂，乙醇作溶剂，研究了丁二烯（Ｂｄ）和丙烯腈（ＡＮ）的溶液共聚合。
2.
The hydroxyl-terminated poly(L-lactic acid) prepolymer is prepared by the melt direct polycondensation process with polyethylene glycol and L-lactic acid,and isocyanate-terminated nitrile rubber(ITBN) is synthesized with toluene-2,4-di-iso-cyanate(TDI),hydroxyl-terminated nitrile rubber(HTBN).
以聚乙二醇和L-乳酸直接熔融缩聚法制备端羟基聚L-乳酸预聚物(HO-PLLA-OH),以甲苯-2,4-二异氰酸酯(TDI)与端羟基丁腈橡胶(HTBN)进行反应,合成了端异氰酸酯基丁腈橡胶(ITBN),然后再将端羟基聚L-乳酸与端异氰酸酯基丁腈橡胶发生偶联反应,合成了乳酸-丁腈橡胶嵌段共聚物,其分子质量高于原料端羟基聚L-乳酸,分子质量分布也比端羟基聚L-乳酸宽。
3) hydroxyl-terminated polybutadiene/acrylonitrile rubber
端羟基液体丁腈橡胶
4) Liquid Hydroxy-Terminated Butadiene-Acrylonitrile (HTBN)
端羟基液态丁腈橡胶(HTBN)
5) carboxyl nitrile rubber
羧基丁腈橡胶
1.
Preparation of powdered carboxyl nitrile rubber/polyvinyl chloride blend;
粉末羧基丁腈橡胶/聚氯乙烯共混胶的研制
2.
In this paper,we choose carboxyl nitrile rubber,polysulfide rubber and hydroxyl polysiloxane as toughners and evaluate the effect of toughened epoxy resin with impact strength,bend strength and tensile shear strength.
以羧基丁腈橡胶、聚硫橡胶和羟基聚硅氧烷为增韧剂,以冲击强度、弯曲强度和拉伸剪切强度来评价环氧树脂的增韧效果。
6) carboxylated nitrile rubber
羧基丁腈橡胶
1.
Vulcanization properties of carboxylated nitrile rubber;
羧基丁腈橡胶的硫化性能
2.
Microphase structure and dynamic mechanical properties of carboxylated nitrile rubber-based damping composites
羧基丁腈橡胶基阻尼复合材料的相态结构及动态力学性能
3.
The blends of chlorosulfonated polyethylene(CSM)and carboxylated nitrile rubber(XNBR) could be vulcanized during molding at 185 ℃× 60 min in the absence of any vulcanizing agent.
在没有任何硫化剂的条件下，氯磺化聚乙烯（ＣＳＭ）和羧基丁腈橡胶（ＸＮＢＲ）的共混物（质量比１∶１）能在１８５℃×６０ｍｉｎ下模压硫化。