1) high temperature sulphidization corrosion
高温硫化腐蚀
2) corrosion by high temperature H 2S
高温硫化氢腐蚀
3) high temperature sulfur corrosion
高温硫腐蚀
1.
Basing on high temperature sulfur corrosion mechanism,the fracture of bolts is a typical stress corrosion cracking(SCC) caused by high temperature and sulfur corrosion.
根据高温硫腐蚀机理分析,确定该连接螺栓的断裂是一起典型的高温硫环境下的应力腐蚀开裂失效案例,主要是由于工作介质中含有硫化氢或者硫蒸汽所致。
2.
This paper explains in detail mechanism of high temperature sulfur corrosion in power plant boilers.
通过阐述锅炉产生高温硫腐蚀的机理,针对实际情况,提出一些预防高温硫腐蚀的具体方法,为火力发电厂采取有效措施,降低受热面高温硫腐蚀情况提供参考。
3.
Heze power plant420 t/h boiler water wall high temperature corrosion belongs to high temperature sulfur corrosion because of the coexistence of sulfate,iron sulfide and hydrogen sulphide corrosion.
菏泽电厂420t/h煤粉锅炉水冷壁发生的高温腐蚀,为硫酸盐、硫化铁、硫化氢3种腐蚀并存,属于高温硫腐蚀类型。
4) high-temperature sulfur corrosion
高温硫腐蚀
5) high temperature corrosion
高温硫腐蚀
1.
With an eye on Huaneng Luohuang Power Plant s 360 MW sets,countermeasures against high temperature corrosion are being explained,among which metal spray coatings have proved themselves to be quite effectiv
高温硫腐蚀是高硫分燃煤锅炉普遍存在的问题,它会引起锅炉受热面泄漏。
6) Sulfidization/Corrosion at high temperature
硫化作用/高温腐蚀
补充资料：高温快速硫化
分子式：
分子量：
CAS号：
性质：指在高于传统硫化温度（134℃左右）下进行的硫化。由于提高硫化温度，必然加快硫化速度、缩短硫化时间、降低能量消耗，同时还能适应橡胶工业生产的自动化、连续化，故是硫化工艺发展的必然趋势。但在高温硫化时，易发生氧化破坏作用，降低硫化胶的物性，为此，应选用合理的硫化体系和耐热性强的胶种，如乙丙橡胶、丁基橡胶、丁腈橡胶、丁苯橡胶等。天然橡胶在高于160℃硫化时，硫化特性变坏，故不宜采用高温硫化。
分子量：
CAS号：
性质：指在高于传统硫化温度（134℃左右）下进行的硫化。由于提高硫化温度，必然加快硫化速度、缩短硫化时间、降低能量消耗，同时还能适应橡胶工业生产的自动化、连续化，故是硫化工艺发展的必然趋势。但在高温硫化时，易发生氧化破坏作用，降低硫化胶的物性，为此，应选用合理的硫化体系和耐热性强的胶种，如乙丙橡胶、丁基橡胶、丁腈橡胶、丁苯橡胶等。天然橡胶在高于160℃硫化时，硫化特性变坏，故不宜采用高温硫化。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条